根据对加拿大部分从事油气管线应力腐蚀破裂(SCC)研究单位的访问考察以及相关资料的调研,以近中性pH SCC为重点,介绍和评述了近年来,特别是1996年以来,有关埋地长输油气管线SCC研究的某些新进展.
参考文献
| [1] | Sridhar N;Dunn D S;Anderko A.Prediction of conditions leading to stress corrosion cracking of gas transmission lines . Environmentally assisted cracking: predictive methods for risk assessment and evaluation of materials[A].equipment,and structures.ASTM STP 1401,R.D.Kane,Ed.,ASTM,2000:241-258. |
| [2] | National Energy Board Public inquiry concerning stress corrosion cracking on Canadian oil and gas pipelines[R].NEB Report MH-2-95, Canada,1996. |
| [3] | King F;Boven G V;Jack T.Predicting the growth of low- and high pH SCC on gas transmission pipelines based on operating conditions[A].Houston: NACE International,2003:127-155. |
| [4] | 刘杏,杨武.天然气长输管线应力腐蚀破裂的敏感环境条件[J].机械工程材料,2002(01):5-12,40. |
| [5] | Chen W;King F;Jack T R et al.Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2002,33:1429-1436. |
| [6] | Beavers J A;Delanty B S;Sutherby R L.Nearneutral pH SCC in susceptible soil environments[A].Houston: NACE International,2001:1217. |
| [7] | Beavers J A;Worthingham R G.The influence of soil chemistry on SCC of underground pipelines[A].Canada: ASME,2000 |
| [8] | Wang SH.;Chen WX. .A study on the pre-cyclic-load-induced burst of creep deformation of a pipeline steel under subsequent static load[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):144-151. |
| [9] | Chen W;Wang S-H.Room temperature creep behavior of pipeline steels and its influence on stress corrosion cracking[A].同文献,ASME,2002:IC2002-27273. |
| [10] | Wang S-H;Chen W;King F .Pre-cyclic-loading-induced stress corrosion cracking of pipelines steels in a near-neutral pH soil environment[J].Corrosion,2002,58(06):526-534. |
| [11] | Chen W;Wang S-H;Chu R.Effect of pre-cyclic-loading on SCC initiation in an X65 pipeline steel exposed to near-neutral pH soil environment[J].Metallurgical and Materials Transactions,2003 |
| [12] | Zheng W;Sutherby R;Revie R W.Stress corrosion cracking of linepipe steels in near-neutral pH environment:[M].a review of the effect of stress,2000:473-483. |
| [13] | Chu R;Chen W;Wang S H.Microstructure dependence of SCC initiation in X65 pipeline steel exposed to a near-neutral pH soil environment[J].Corrosion,2003 |
| [14] | Lu B;Luo J;McCrady B.Near-neutral pH SCC initiation and early propagation of X70 pipeline steel[M].(同文献[7]) . ASME,2002:IC2002-27234. |
| [15] | Bulger J;Luo J.Effect of microstructure on nearneutral Ph SCC[A].IPC.ASME,2000:947-952. |
| [16] | Parkins R N.Laboratory measurements and life prediction for structures suffering stress corrosion cracking . Proceedings of international symposium on plant aging and life predictions of corrodible structures[M].Sapporo, Japan: NACE International,1997:1-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%