采用柠檬酸盐溶胶-凝胶法来获得高温氢气氛下的氢传感器材料BaCe0.95Yb0.05O3-α固体电解质前驱粉体.利用同步差热-热重分析仪,X射线衍射仪(XRD),透射电镜(TEM)和扫描电镜(SEM)对样品进行测试和表征.结果表明:溶胶凝胶法最终形成单一的钙钛矿相结构前驱粉体温度约为850℃,比固相反应法合成温度降低了约400～600℃,比液相草酸盐共沉淀法降低了约150～400℃,避免了微波合成法合成时间过短,杂质较多的缺点.同时得到的粉体粒径小、颗粒均匀、分散性好,易于烧结且致密.
参考文献
| [1] | 肖恺,闫一功,雷良才,杜元龙.固态电解质氢传感器的研究进展[J].腐蚀科学与防护技术,2001(03):165-168. |
| [2] | Iwahara H;Esaka T;Uchida H.Proton conduction in sintered oxides and its application to steam electrolysis for hydrogen production[J].Solid State Ionics,1981(3-4):359-363. |
| [3] | Iwahara H;Uchida H;Ono K.Protonic and oxide ionic conduction in BaCeO3-based ceramics-effect of partial substitution for Ba in BaCe0.9O3 with Ca[J].Journal of the Electrochemical Society,1988(135):529-532. |
| [4] | Mitsui A;Miyayama M;Yanagida H.Evaluation of the activation energy for proton conductionin perovskite-type oxides[J].Solid State Ionics,1987(32):213-217. |
| [5] | Yajima T;Suzuki H;Yogo T.Protonic conduction in SrZrO3-based oxides[J].Solid State Ionics,1992(51):101-107. |
| [6] | Yajima T;Kazeoka H;Yogo T.Proton conduction in sintered oxides based on CaZrO3[J].Solid State Ionics,1991(47):271-275. |
| [7] | 马桂林.Ba0.95Ce0.90Y0.10O3-α固体电解质的质子导电性[J].无机化学学报,1999(06):798-802. |
| [8] | 于化龙;陈威;王常珍 .BaCe0.95Y0.05O3-α固体电解质材料的热性质[J].东北大学学报(自然科学版),1995,16(01):21-23. |
| [9] | 李光强;郭振中 等.湿化学法制备CaZr1-xInxO3-α及其烧结体的阻抗谱研究[J].硅酸盐学报,1996,24(04):430-434. |
| [10] | 徐秀廷.SrCeO3的微波合成及离子导电性质研究[J].高等学校化学学报,1996(10):1519. |
| [11] | 何志奇;蒋凯.BaCe1-xRExO3-05x的溶胶-凝胶法合成及离子导电性[J].应用化学,1998(15):22-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%