测试了研制的绿色缓蚀剂在中性3.5%NaCl水溶液中抑制3种钢的应力腐蚀开裂(SCC)和腐蚀疲劳(CF)断裂的能力,结果表明抑制SCC的能力超过铬酸盐、磷酸盐的水平,抑制CF的能力则与研制缓蚀剂的配方有关.
参考文献
| [1] | Kenjiro Komai .Failure analysis and prevention in SCC and corrosion fatigue cases[J].International Journal of Fatigue,1998(2):145-154. |
| [2] | Woodtli J.;Kieselbach R. .Damage due to hydrogen embrittlement and stress corrosion cracking[J].Engineering failure analysis,2000(6):427-450. |
| [3] | 左景伊.应力腐蚀破裂[M].西安:西安交通大学出版社,1985:158-160. |
| [4] | 黄彦良.缓蚀剂对316L不锈钢在酸性氯离子溶液中应力腐蚀开裂的作用[J].腐蚀科学与防护技术,1993(03):192. |
| [5] | Nishimura R;Sundjono .Effect of chromate and molybdate on stress corrosion cracking of type 304 austenitic stainless steel in hydrochloric acid solution[J].Corrosion,2000,56(04):361-370. |
| [6] | V. V. Panasyuk;L V. Ratych .Inhibitor Protection of Metals at the Corrosion Fatigue Crack Growth Stage[J].Corrosion: The Journal of Science and Engineering,1995(4):284-294. |
| [7] | 化学工业部化工机械研究所.耐蚀金属材料与防蚀技术分册[M].北京:化学工业出版社,1990:1021-1025. |
| [8] | 黄淑菊,刘斌,孔繁鹏,顾美转,孔丽青.钢的绿色防锈抑断缓蚀剂的研制Ⅰ--在3.5%NaCl水溶液中的防锈性能[J].腐蚀与防护,2004(12):517-519. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%