根据锌在户外典型地区大气腐蚀的特点,研究了模拟户外大气环境的实验室加速腐蚀试验方法,且从腐蚀动力学特征、腐蚀机理、腐蚀产物及试样表观干湿状态四方面探讨了锌在我国典型地区大气暴露腐蚀试验结果与实验室加速腐蚀试验结果的相关性.研究结果表明,SO2/盐雾复合循环加速腐蚀试验一定程度上较好地模拟了锌在典型地区的大气腐蚀行为,通过这种加速腐蚀试验可以针对锌在典型地区大气暴露腐蚀行为进行一定程度的预测.
参考文献
| [1] | Boelen B .A literature survey on the development of an accelerated laboratory test method for atmospheric corrosion of precoated steel produces[J].Corrosion Science,34(11):1923-1931. |
| [2] | ZHANG X G .Corrosion ratios of steel to zinc in natural corrosion environments[J].Corrosion,1999,55:124-126. |
| [3] | James Maxted .Shorttermtestingandrealtimeexposure[R].Corrosion Paper,1999. |
| [4] | Granese S L.Behaviour of Zn in atmospheres containing sulphur dioxide and chloride ions[A].:2. |
| [5] | Feliu S;Morcillo M .The prediction of atmospheric corrosion from meteorological and pollution parameters[J].Corrosion Science,1993,34(03):403-414. |
| [6] | Antonio R;Mendoza;Francisco Corvo.Outdoor and indoor atmospheric corrosion of non-ferrous metals[J].Corrosion Science,2000(42):1123-1147. |
| [7] | 王绍明,萧以德,张三平.锌及锌覆盖层户外大气暴露腐蚀行为的研究[J].材料保护,2004(11):24-26. |
| [8] | Odnevall I;LeygrafC .The Formation of Zn4SO4(OH)6*4H2O in a rural atmosphere[J].Corrosion Science,1994,36(06):1077-1091. |
| [9] | Odnevall I;LeygrafC .Formation of NaZn4Cl(OH)6SO4*6H2O in a marine atmosphere[J].Corrosion Science,1993,34:1213-1229. |
| [10] | Odnevall I;LeygrafC .The formation of Zn4Cl2(OH)4SO4@5H2O in a urban aand industrial atmosphere[J].Corrosion Science,1994,36(09):1551-1567. |
| [11] | 严川伟,史志明,林海潮,曹楚南.Zn在SO2环境中大气腐蚀初期表面特性研究[J].腐蚀科学与防护技术,2000(03):151-153. |
| [12] | 王振尧;于国才;郑逸苹 等.锌的加速腐蚀与大气暴露腐蚀的相关性研究[J].中国腐蚀与防护学报,1999,19(04):239-244. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%