用恒变形U形弯曲试样应力腐蚀试验研究了长期服役在650～720℃下的316L奥氏体不锈钢室温下在0.38mol/L连多硫酸溶液及0.38mol/L连多硫酸+0.5mg/L NaCl溶液中的应力腐蚀破裂(SCC)行为.采用金相显微镜(OM)、扫描电子显微镜(SEM)对裂纹形态、断口形貌进行观察和分析.结果表明,该钢在0.38mol/L连多硫酸溶液中没有发生应力腐蚀破裂现象,而在0.38mol/L连多硫酸+0.5mg/L NaCl溶液中发生了应力腐蚀破裂,裂纹扩展为混合型,氯离子对钢表面钝化膜的破坏是诱发应力腐蚀破裂的主要原因之一.
参考文献
| [1] | Rokuro Nishimura;Achmad Sulaiman;Yasuaki Maeda .Stress corrosion cracking susceptibility of sensitized type 316 stainless steel in sulphuric acid solution[J].Corrosion Science,2003,45:465-484. |
| [2] | Rokuro Nishimura;Iing Musalam;Yasuaki Maeda .The effect of sensitizing temperature on stress corrosion cracking of type 316 austenitic stainless steel in hydrochloric acid solution[J].Corrosion Science,2002,44:1343-1360. |
| [3] | 陈浩,王燕斌,褚武扬,高克玮,乔利杰.氢致马氏体对304不锈钢在MgCl2中应力腐蚀的影响[J].金属学报,2002(10):1079-1081. |
| [4] | Marc Vankeerberghen;Digby D Macdonald .Predicting crack growth rate vs. temperature behavior of type 304 stainless steel in dilute sulphuric acid solutions[J].Corrosion Science,2002,44:1425-1441. |
| [5] | 李金许,高克玮,宿彦京,王燕斌,乔利杰,褚武扬.钝化膜应力导致不锈钢应力腐蚀的研究[J].中国科学E辑,2003(09):796-803. |
| [6] | 许淳淳,张新生,胡钢.拉伸变形对304不锈钢应力腐蚀的影响[J].材料研究学报,2003(03):310-314. |
| [7] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:46. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%