利用自腐蚀电位测定、线性极化、阳极极化、交流阻抗等试验方法对JT345经济型耐大气腐蚀钢的锈层和裸钢进行研究,与Q235B及CortenA钢对比了它们的耐大气腐蚀性能和规律.电化学试验表明,大气腐蚀过程中生成的锈层使电化学阳极过程受到显著的阻滞.从热力学上看,自腐蚀电位正移320mV以上;从动力学上看,锈层表面趋于钝化,阳极电流降低两个数量级以上.
参考文献
| [1] | 于福洲.金属材料的耐蚀性[M].北京:科学出版社,1982 |
| [2] | Larrabee C P;Cobum S K.First international congress on metallic corrosion[M].London,1961:276. |
| [3] | 国家自然科学基金重大项目:材料自然环境腐蚀"八五"数据汇编[Z].,1996. |
| [4] | 侯文泰;于敬敦;梁彩凤 .碳钢及低合金钢的大气腐蚀[J].中国腐蚀与防护学报,1993,13(04):291. |
| [5] | 侯文泰;梁彩凤 .经济耐候钢[J].钢铁研究学报,1994,6(02):40. |
| [6] | 鹿岛和幸;岸川浩史 .Evaluation of rust layer on weathering steel[J].材料与工艺,1998,11(06):1108. |
| [7] | Masahiro Yamamoto;Toshiaki Kodama .Transition of research on weathering steels and development of new weathering steels[J].ふぇらむ,1999(3):155-162. |
| [8] | 刘丽宏,齐慧滨,卢燕平,李晓刚.耐候钢的腐蚀及表面稳定化处理技术[J].腐蚀与防护,2002(12):515-518. |
| [9] | Yamashita M;Miyuki H;Matsuda Y.The long term growth of protective rust layer formed on weathering steel by atmospheric corrosion during quarter of a century[J].Corrosion Science,1994(02):283-299. |
| [10] | 托马晓夫H.Л;华保定X.金属腐蚀及其保护理论[M].北京:中国工业出版社,1964:1. |
| [11] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,1985:190. |
| [12] | 宋诗哲.腐蚀电化学研究方法[M].北京:化学工业出版社,1988:107. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%