研制了一种气相防锈涂料,主要由热塑性丙烯酸树脂、气相缓蚀剂(VCI)、增韧剂、抗氧化剂、抗菌防霉剂、有机溶剂等组成.把含不同VCI的涂料喷涂在标准邮政纸盒上,金属试片20#钢、45#钢、A3钢和炮钢分别粘在纸盒的上方,室温下进行不同时间的预膜,然后盒中放入电解质溶液,加热进行加速试验.结果表明相同的预膜时间、相同的金属试片,随着涂料中VCI含量的增加防锈效果越好;相同的VCI含量,随着预膜时间的延长防锈效果越好.