通过对新型Al-Cu-Li系合金腐蚀的不同时间的电化学阻抗谱(EIS)分析,研究了该合金在T6、T8两种状态的腐蚀行为.宏观腐蚀行为和电化学阻抗谱表明,T8态由于时效前的预变形有效地降低了合金的腐蚀敏感性.从未经腐蚀的材料的微观形貌分析了该合金晶界、亚晶界和相关的第二相的分布和形貌进一步解释了两种状态合金腐蚀行为的差异性.T8态存在大量界面,使倾向于在晶界亚晶界形核的T1相在基体中分布较T6态细小,在剥落腐蚀中由腐蚀产物形成的楔形力较小,因此,T8态表现出比T6态更好的抗腐蚀能力.
参考文献
| [1] | 李劲风,郑子樵,任文达.第二相在铝合金局部腐蚀中的作用机制[J].材料导报,2005(02):81-83,90. |
| [2] | 李劲风,张昭,曹发和,程英亮,张鉴清,曹楚南.Al-Li合金在EXCO溶液中腐蚀的电化学阻抗研究[J].金属学报,2003(04):426-430. |
| [3] | Conde A;de Damborenea J .Evaluation of exfoliation susceptibility by means of the electrochemical impedance spectroscopy[J].Corrosion Science,2000,42:1393. |
| [4] | Conde A;de Damborenea J .Characterization of the SCC behaviour of 8090 Al-Li alloy by means of the slow-strain-rate technique[J].Corrosion Science,1998,40(01):91. |
| [5] | Conde A;Damborenea J de .An electrochemical impedance study of a natural aged Al-Cu-Mg alloy in NaCl[J].Corrosion Science,1997,39(02):285-303. |
| [6] | Cao C N Wang J;Lin H C .Features of AC impedance of pitting corroded electrodes during pits propagation[J].Chin Soc Corros Prlt,1989,9:261. |
| [7] | 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:北京科学技术出版社,2002 |
| [8] | 张匀;刘玉林;赵洪恩 等.8090Al-Li合金晶间腐蚀与剥落腐蚀性能研究[J].金属学报,1991,21(04):B271. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%