采用电解充氢方法对2.25Cr-1Mo钢氢致裂纹扩展进行试验,并采用甘油测氢法测定了2·25Cr-1Mo钢发生裂纹扩展时钢中扩散的平均氢浓度.为了进一步了解裂纹尖端的氢浓度大小对裂纹扩展的影响,利用有限元软件对氢在2.25Cr.1Mo钢中的扩散过程进行模拟分析,系统研究了在应力-氢环境交互作用下裂纹尖端周围的氢扩散规律,并给出了裂纹扩展时裂尖局部位置的氢浓度大小.
参考文献
| [1] | 化工部化工机械研究所.腐蚀与防护手册(腐蚀理论、试验及监测)I-M3[M].北京:化学工业出版社,1989 |
| [2] | A Nagao;S Kuramoto;K Iehitani.Visulization of hydrogen transport in high strength steels affected by stress fields and hydrogen trapping[J].Scripta Mater,2001(45):1227-1232. |
| [3] | R D Smith Ⅱ;G P Landis;I Maroef.The de termination of hydrogen distribution in high-strength steel weldments Partl:laser ablation methods[J].Welding Journal,2001(05):41-46. |
| [4] | Zhengdong Wang;Li Hua;Dongdi WtL.Simulation of hydrogen-induced cracking in reactor steels[A].上海:华东科技大学出版社,2003 |
| [5] | 董金梅,林建鸿,王正东.加氢反应器氢致开裂的有限元分析[J].压力容器,2001(03):47-49. |
| [6] | Hong Xu;Li Hua;Xiang-ming Xia .Experimental study of temper embrittlement of aged specimens removed from a hydrogenation reactor[J].Engineering failure analysis,2006(4):615-623. |
| [7] | 徐颖.电解充氢试验条件对堆焊层剥离的影响[J].压力容器,1993(06):7. |
| [8] | 褚武扬.氢损伤和滞后断裂[M].北京:冶金工业出版社,1988:57-58. |
| [9] | 庄茁;张帆;岑松.ABAQUS非线性有限元分析实例[M].北京:科学出版社,2005 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%