HP40钢表面沉积Al2O3薄膜及其抗结焦性能

1.华东理工大学,上海,200237

2.华东理工大学,上海,200237

3.华东理工大学,上海,200237

4.华东理工大学,上海,200237

5.华东理工大学,上海,200237

Steel HP40 Coated by Alumina Film and Its Anticoking Ability

采用金属有机化学气相沉积法(MOCVD)在HP40)钢表面制备了Al2O3薄膜,通过EDS能谱分析和扫描电镜(SEM)测试分析了涂层的微观组织和表面形貌.结果表明,该薄膜在乙烯裂解的高温条件下抑制结焦率为65%左右,Al2O3薄膜大大提高了HP40钢的抗结焦能力.

[1]	黄志荣.乙烯裂解结焦机理及结焦抑制技术进展[J].江苏石油化工学院学报,2000(02):36-39.
[2]	黄贤平.乙烯裂解炉结焦控制技术近况[J].江苏化工,2004(02):49-51,58.
[3]	Hall D J;Hossain M K;Atkinson R F .Carburisation behaviour of HK40 steel in furnaces USed for ethylene production[J].High Temperature and High Pressure,1982,14:527-553.
[4]	Kang S C .Method of on-line coating of a film on the inner walls of the reaction tubes in a hydrocarbon py rolysis reactor[P].US 2003/0152701A1,2003-8-14.
[5]	车俊铁,李玉珠.HK40和HP40高温炉管材料性能对比分析[J].工业炉,2004(04):4-6.
[6]	吴欣强 .新型抗结焦裂解炉管材料的设计、制备与性能[D].中国科学院金属研究所,1999.
[7]	C S Li;Y S Yang .A glass based coating for enhan cing anti-coking and antkearburming abilities of heat resistant steel HP[J].urface＆Coatings Technology,2004,185:68-73.

上一张下一张

计量

作者相关

文章评分