针对海洋环境钢筋混凝土构筑物过早腐蚀破坏,从混凝土防护、钢筋保护、包覆隔离保护、施工技术四个方面综述目前国内外对海洋环境下保护钢筋减少腐蚀、延长构筑物服役寿命所采取的技术措施,内容涉及:高性能混凝土、抗海水腐蚀水泥、阻锈剂、混凝土表面涂层、提高保护层厚度、钢筋涂层、耐腐筋、电化学保护、纤维玻璃钢或钢护筒包覆隔离、预防早期开裂、透水模板.重点讨论各措施的基本原理、特点、主要缺点和发展方向及工程应用.其中海工高性能混凝土是最经济、最基本和不可替代的,其他作为高性能混凝土基本措施的有效补充.
参考文献
| [1] | 陆儒德.海洋·国家·海权[M].北京:海潮出版社,2000:135-180. |
| [2] | 陈惠民.加快技术创新,促进我国海洋工程开发[J].中国海洋平台,1999(03):4-7. |
| [3] | QIU D H;WANG Y X .Developing tendency of coastal and offshore engineering in the 21st century[J].Progress in Natural Science,2000,10(06):425-431. |
| [4] | Wall bank E J .The Performance of concrete in bridges:a survey of 200 highway bridges[R].London:HMSO,1989. |
| [5] | Broomfield.Corrosion of steel in concrete:understanding,investigating and repair[M].E & FN SPON,1997 |
| [6] | 范卫国;潘今岱;罗德宽.北仑港码头钢筋混凝土上部结构腐蚀破坏调查报告[A].陕西西安,1997 |
| [7] | High performance concrete handbook-materials and applications[M].Swedish,1998 |
| [8] | Whitman F H;Schwesinger P;冯乃谦.High performance concrete material properties and designer[M].北京:中国铁道出版社,1998 |
| [9] | 安明喆,朱金铨,覃维祖.高性能混凝土的自收缩问题[J].建筑材料学报,2001(02):159-166. |
| [10] | 吴中伟.高性能混凝土(HPC)发展趋势[J].建筑技术,1998(01) |
| [11] | 李乃珍;李启棣.抗海水水泥对高硫酸盐、氯离子的耐腐蚀性能及其机理[J].中国建材科技,1998(05):7-13. |
| [12] | 李启棣;吴淑华.硫铝酸盐水泥混凝土的特性及应用[M].北京:中国铁道出版社,1989 |
| [13] | 洪乃丰.钢筋阻锈剂的应用和长期有效性[J].工业建筑,1993(05):42. |
| [14] | 王嵬,张大全,张万友,周国定.国内外混凝土钢筋阻锈剂研究进展[J].腐蚀与防护,2006(07):369-373. |
| [15] | Edelman A;Miksic B;Gelner L.Migrating corrosion inhibitors for reinforced concrete[J].Com Chem Journal,1993(02):38-43. |
| [16] | Miksic B;FelnerL;Bjegovic D.Migrating corrosion inhibitors for reinforced concrete[A].Ferrara,1995:569-588. |
| [17] | A. A. Almusallam;F. M. Khan;S. U. Dulaijan .Effectiveness of surface coatings in improving concrete durability[J].Cement & concrete composites,2003(4/5):473-481. |
| [18] | IbrahimM;Al-Gahtani AS;Maslehuddin Ml .Effectiveness of concrete surface treatment materials in reducing chloride-induced reinforcement corrosion[J].Construction and Building Materials,1997,11(7-8):443-451. |
| [19] | ACI201-Guide to Durable Concrete[M].,1998 |
| [20] | 王胜年,潘德强,卫淑珊,黄君哲.海工混凝土的长期耐久性研究[J].水运工程,2001(08):20-22. |
| [21] | DIAMONDS .Corrosion behavior of steel building materials[J].Cement and Concrete Research,1981,11(03):383-394. |
| [22] | LAMBERTC .Protection of concrete[J].British Corrosion Journal,1995,30(01):8. |
| [23] | 吴金岳,吴松贵,徐旭峰,徐乃欣.环氧涂层钢筋及其应用[J].腐蚀与防护,2004(03):105-108. |
| [24] | 杜洪彦,邱富荣,许世力,余兴增,石小燕.海上混凝土防腐蚀涂料研究进展[C].第五届全国建筑腐蚀防护学术交流会论文集,2000:32-34. |
| [25] | NACE Standard RP 0390-1990.NACE Standard RP 0390-1990.Maintenance and rehabilitation considerations for corrosion control existing steel reinforcedconcrete structures,NACE international[S].Houston,Texas,USA |
| [26] | Baroghel-Bouny V;Godin J;Gawsewitch J.Microstructure and moisture properties of high-performance concrete[A].Paris:RILEM,1996:451-461. |
| [27] | 祝昌暾,陈敏,杨杨,欧新新,陈飞云.高强混凝土的收缩和早期徐变特性[J].混凝土与水泥制品,2005(02):1-4. |
| [28] | Robert Springenschmid.Avoid of thermal cracking in concrete at early ages[M].RILEM Technical Committee,1998 |
| [29] | 朱伯芳.大体积混凝土温度应力与温度控制[M].北京:中国电力出版社,1999 |
| [30] | 任玉杰.透水模板对提高混凝土耐久性的实验研究[J].港口工程,1995(01) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%