报道了新开发的纳米晶Fe72.5Cu1Nb1.5Mo1.5V1Si13.5B9合金的综合磁性能.新合金的直流起始磁导率和矫顽力水平分别达到13×104和0.64Am-1.在Bm＝0.3T,f＝100kHz和Bm＝0.2T,f＝200kHz条件下,铁损分别为578kW.m-3和884kW.m-3,这可与纳米晶Fe73.5Cu1Nb3Si13.5B9合金的相比,但比优良的功率Mn-Zn铁氧体H7C4的低得多.在Bmf＝(10～40)T.kHz条件下,在f＝(20～6000)kHz范围内,描述了铁损、相应幅值磁导率和动态矫顽力的行为.
参考文献
| [1] | Yoshizawa Y;Yamauchi K .[J].Journal of Applied Physics,1988,64:6044. |
| [2] | Zhang Y Z;Nian S Z .[J].Acta Metall Sin,1992,5:502. |
| [3] | Zhang Y Z .[J].J Mater Sci Technol,1997,13:425. |
| [4] | Zhang Y Z .[J].Acta Metall Sin(English Letter),1997,10:489. |
| [5] | Zhang Y Z .[J].J Mater Sci Technol,1998,14:538. |
| [6] | 张延忠 .[J].功能材料与器件学报,1997,3:162. |
| [7] | Zhang Y Z .[J].J Mater Sci Technol,1999,15:83. |
| [8] | Fuxishaki K .[J].Electro Eng,1989,31:116. |
| [9] | 廖绍彬.铁磁学[M].北京:科学出版社,1988:15. |
| [10] | Knobel M.;Gomezpolo C.;Marin P.;Vazquez M.;Hernando A.;Sanchez ML. .GIANT MAGNETO-IMPEDANCE EFFECT IN NANOSTRUCTURED MAGNETIC WIRES[J].Journal of Applied Physics,1996(3):1646-1654. |
| [11] | Mulhall B E .[J].Proceedings of The IEEE,1964,11:183. |
| [12] | Schafer R et al.[J].Journal of Applied Physics,1991,69:5325. |
| [13] | 王桂英.电源变换技术[M].北京:人民邮电出版社,1990:405-408. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%