用磁天平(MB)及提拉样品磁强计(ESM)研究了(Fe1-xCox)84Zr3.5Nb3.5B8Cu1(x＝0～0.8)非晶合金高温与低温磁性的变化,结果表明,该非晶态合金加热到800～900℃后,除x＝0.8的合金外,合金的室温饱和磁化强度均比淬态有所提高;X射线衍射的结果表明,x＝0,0.2,0.4,0.6的合金中析出单一的α-Fe(Co)相,x＝0.8的合金中析出Co3B,FeB相,当x＝1.0时合金中析出单一的fcc Co相.该非晶合金在1.5K时的饱和磁化强度σs随Co含量的增加先增大,当x＝0.2时达到最大值,然后随着x的增大,合金的σs逐渐下降.
参考文献
| [1] | Yoshizawa Y;Oguma A;Yamauchi K .[J].Journal of Applied Physics,1988,64:6044. |
| [2] | Fujii Y;Fujita H;Seki A;Tomida T .[J].Journal of Applied Physics,1991,70:6241. |
| [3] | Makino A;Suzuki K;Inoue A;Masumoto T,Mater Tran .[J].Materials Transactions-Japan Institute of Metals,1991,32:551. |
| [4] | Suzuki K;Makino A;Inoue A;Masumoto T .[J].Journal of Applied Physics,1993,74:3316. |
| [5] | Makino A;Hatanai T;Yoshida S;Hasegawa N,Inoue A,Masumoto T .[J].Science Reports Tohoku University,1996,A42:121. |
| [6] | Beach R S;Berkowikz A E .[J].Applied Physics Letters,1994,64:3652. |
| [7] | 贺淑莉 .[D].沈阳:东北大学,1997. |
| [8] | Weiss P;Forrer R .[J].Annals of Physics,1929,12:279. |
| [9] | Mizoguchi T;Yamauchi K;Miyajima H.[A].Hooper and Graaf,Plenum Press,1973:325. |
| [10] | 詹文山;沈保根;赵见高 .[J].物理学报,1985,34:1613. |
| [11] | 沈保根,詹文山,赵见高,陈金昌.非晶态Fe90-xBxZr10合金的磁性、电性和晶化[J].物理学报,1986(07):841-849. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%