采用粉末冶金法制备多孔镁,孔隙率可在20%到55%范围内变化,并研究了多孔镁的压缩性能和抗弯强度与孔隙率之间的关系.结果表明,多孔镁的孔隙率、孔径可通过造孔剂的含量和粒度来控制,随着孔隙率的增加,抗压强度和杨氏模量变小,抗弯强度下降;采用粉末冶金方法制备的多孔生物镁不论是从压缩强度,杨氏模量还是从抗弯强度上来讲,都可以满足移植材料的要求.
参考文献
| [1] | Davies G J.[J].Journal of Materials Science,1983(18):1899. |
| [2] | 汤慧萍,张正德.金属多孔材料发展现状[J].稀有金属材料与工程,1997(01):1-6. |
| [3] | Gibson L F.Cellular Solids:Structure and Properties[M].Cambridge:Cambridge University Press,1997 |
| [4] | Evans A G;Hutchinson J W;Ashaby M F.[J].Progress in Materials Science,1999:43-171. |
| [5] | 浦素云.金属植入材料及其腐蚀[M].北京:北京航空航天大学出版社,1990 |
| [6] | Zitelli JP;Higham P A .[J].Materials Research Society Symposium Proceedings,2000,599:117. |
| [7] | Jiang Shuwen;Qi Min .[J].Materials Science and Engineering,2002,20:597. |
| [8] | Nakajima H;Hyun S K;Oashi K.[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2001(09):179. |
| [9] | 宝鸡有色金属研究所.粉末冶金多孔材料[M].北京:冶金工业出版社,1979 |
| [10] | Wen C E;Yamada Y et al.[J].Materials Letters,2004,58:357. |
| [11] | 杨定焯,杨惠,刘芳,张倩,王文志.力学负荷对峰值骨量影响的初步研究[J].中国骨质疏松杂志,2003(02):124-127. |
| [12] | Wen C E;Mabuchi M et al.[J].Scripta Materialia,2001,45:1147. |
| [13] | Lorna J Gibson;刘培生.多孔固体结构与性能[M].北京:清华大学出版社,2003 |
| [14] | Chang Y S;Oka M et al.[J].Biomaterials,1995,16:1. |
| [15] | LONG M H J .[J].Biomaterials,1998,19:1621. |
| [16] | Gibson L G.Cellular Solids:Structure and Properties[M].Cambridge Univ Press,UK,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%