利用X射线衍射(XRD)和差热分析(DSC)方法试验研究了Nb元素对Fe-(Al,Ga)-(P,C,Si,B)系合金非晶晶化的影响.结果表明:Fe73Nb1Al4Ga2P12B4Si4的晶化过程为α-Fe→α-Fe+Fe5SiP+Al0.7Fe3Si0.3+Fe3B+剩余非晶化相;替代元素Nb的加入提高了材料的晶化温度,改变了Fe74Al4Ga2P12B4Si4的晶化激活能,其中形核激活能(Eg)、晶化起始激活能(Ex)和第一晶化峰激活能(Ep1)都大大增加;另外,Nb的加入还使合金晶化后的晶粒尺寸大大减小.
参考文献
[1] | Inoue A;Gook Y S .[J].Materials Transactions-Japan Institute of Metals,1995,36:1180. |
[2] | Hono K et al.[J].Acta Metallurgica Et Materialia,1992,40(09):2137. |
[3] | Koster U et al.[J].MATERIAL SCIENCE AND ENGINEERING,1991,A133:611. |
[4] | 杨会生;张寿禄 .[J].科学通报,1993,38(19):1244. |
[5] | Chnuma M.[J].ACTA MATERIALIA,2000(48):4783. |
[6] | Chen W Z;Ryder P L.[J].MATERIAL SCIENCE AND ENGINEERING,1995(B3):4204. |
[7] | Ayers J D;Harris V G et al.[J].Acta Materialia,1998,46(06):1861. |
[8] | Herold U;Koster U.[A].Brighton (Metals Society,London),1978:281. |
[9] | de Boor F R;Boom R.Cohesion in metals[M].AMSTERDAM:ELSEVIER,1988 |
[10] | Inoue A;Zhang T .[J].Journal of Non-Crystalline Solids,1999,250-252:552. |
[11] | Inoue A .[J].MATERIALS SCIENCE FORUM,1999,312-314:307-314. |
[12] | 殷俊林,尤富强,高国华,王景成.非晶软磁合金薄带纳米晶化过程中缺陷变化的正电子湮没研究[J].热处理,2003(03):16-20. |
[13] | Inoue A .[J].Acta Materialia,2000,48:279. |
[14] | Luborsky F E;Walter J L .[J].Journal of Applied Physics,1976,47(03):3648. |
[15] | 曲哲 等.[J].金属学报,1990,26(05):B331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%