采用矿相显微镜及XRD研究了不同温度条件下连铸保护渣矿相结构的变化.结果表明,在本实验条件下的降温和升温过程中,连铸保护渣的结晶化率均随实验温度的升高而下降,结晶矿相主要为枪晶石、硅灰石、黄长石.枪晶石在1 000 ℃和1 200 ℃时结晶能力最强,1 300 ℃时无枪晶石析出.硅灰石只在1 000 ℃时析出,晶体发育程度很高.黄长石晶体在1 300 ℃时发育良好且光学性质明显,1 000 ℃和1 200 ℃时生长缓慢,为细小的颗粒状雏晶.在相同的实验温度条件下,连铸保护渣在升温过程中结晶化率高、晶体细小、结构致密,降温过程中其晶体发育程度良好、晶体粗大.
参考文献
| [1] | 舒俊,金山同,张丽,曹卫文,宋任波,王向光.连铸保护渣结晶矿相的研究[J].钢铁,2001(09):21-24. |
| [2] | 朱传运,刘承军,史培阳,姜茂发.保护渣成分对结晶矿相的影响[J].东北大学学报(自然科学版),2004(06):559-562. |
| [3] | 迟景灏;甘记年.连铸保护渣[M].沈阳:东北大学出版社,1993 |
| [4] | J. A. Kromhout;V. Ludlow;S. McKay .Physical properties of mould powders for slab casting[J].Ironmaking & Steelmaking: Products and applications,2002(3):191-193. |
| [5] | P. R. Scheller .Interfacial phenomena between fluxes for continuous casting and liquid stainless steel[J].Ironmaking & Steelmaking: Products and applications,2002(2):154-160. |
| [6] | P. R. Scheller .Interfacial phenomena between fluxes for continuous casting and liquid stainless steel[J].Ironmaking & Steelmaking: Products and applications,2002(2):154-160. |
| [7] | Billany T J H .Surface Cracking in Continuously Cast Products[J].Ironmaking and Steelmaking,1991,18(06):403. |
| [8] | 王谦,王雨,谢兵,迟景灏.合金钢连铸结晶器保护渣的基本功能[J].特殊钢,2004(01):1-4. |
| [9] | Yamauchi A .Heat Transfer Between Mold and Strand Through Mold Flux Film in Continuous Casting of Steel[J].ISIJ International,1993,33(01):140. |
| [10] | 饶东生.硅酸盐物理化学[M].北京:冶金工业出版社,1996 |
| [11] | 董方,王艺慈,王宝峰.高速连铸结晶器保护渣渣膜凝固结晶组织研究[J].炼钢,2006(05):43-45,51. |
| [12] | 魏国强,徐涛,于学斌.冷却水对结晶器铜管使用寿命影响的研究[J].河南冶金,2002(01):18-20. |
| [13] | 谢延敏,于沪平,阮雪榆,王宝峰,麻永林.小方坯高速连铸结晶器温度场和应力场的有限元模拟[J].铸造,2004(09):727-731. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%