使用一专门设计的模型制作了碳化硅(Nicalon)/玻璃复合材料单纤维拉出试样.利用纤维拉曼峰波数偏移与纤维所受应变的近似线性关系,首先测定纤维热残余应变的分布,随后对伸出玻璃基体外的纤维段施加给定的拉伸应变, 沿纤维轴向用拉曼光谱术逐点测定基体内外纤维的应变,最后依据力平衡原理将应变分布转换为界面剪切应力沿纤维轴向的分布.结果表明:在给出的实验参数下,界面传递应力长度为0.18 mm,最大界面剪切应力的位置在x为0.11 mm处.
参考文献
| [1] | Griffin C W;Limaye S Y;Richerson D W;Shetty D K .[J].Ceramic Engineering and Science Proceedings,1988,9:671-678. |
| [2] | Goettler E W;Faber K T .[J].Journal of Computer Science and Technology,1989,37:129-147. |
| [3] | Batler E P;Fuller E R;Chan H M.In tailored interfaces in composite mater ials[A].PA:Mat Res Soc,1990:170，17-24. |
| [4] | Goettler R W;Faber K T .[J].Ceramic Engineering and Science Proceedings,1988,9:861-870. |
| [5] | Bright J D;Danchaivijtt S;Shetty D K .[J].Journal of the American Ceramic Society,1991,74:115-122. |
| [6] | Deshmukh U V;Coyle T W .[J].Ceramic Engineering and Science Proceedings,1988,9:627. |
| [7] | Yang X;Young R J .[J].Composites,1994,25:488-493. |
| [8] | Yang X;Young R J .[J].British Ceramic Transactions,1994,93:1-10. |
| [9] | Yang X;Young R J .[J].Journal of Materials Science,1993,28:2536-2544. |
| [10] | 杨序纲;王依民 .[J].材料研究学报,1996,10:628-632. |
| [11] | Yang X;Young R J .[J].Acta Metallurgica Et Materialia,1995,43:2407-2415. |
| [12] | Yang X;Young R J .[J].Composites Part A:Applied Science and Manufacturing,1996,27:737-741. |
| [13] | Kelly A;Macmllan N H.Strong Solids[M].Oxford:Clarendon Press,1986:251. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%