研究了两种不同磷含量化学镀镍层的组织结构、硬度及弹性模量,并着重研究了30CrMo及LY12经化学镀镍后的旋转弯曲疲劳性能.结果表明,低磷微晶镀层较高磷非晶镀层具有更高的硬度、弹性模量和疲劳抗力;化学镀镍层导致了30CrMo疲劳强度的显著下降,但能提高LY12的疲劳强度,表明化学镀镍层对基体疲劳性能的影响作用主要取决于基体本身疲劳抗力的高低.
参考文献
| [1] | Keene R H .[J].Plating and Surface Finishing,1988,75(12):22. |
| [2] | Tulsi S S .[J].Transactions of The Institute of Metal Finishing,1986,64:73. |
| [3] | Tagami M et al.[J].Japanese Journal of Institute of Light Metals(Japan),1993,43(05):281. |
| [4] | 张永忠 等.[J].宇航材料工艺,1998,28(01):52. |
| [5] | 张永忠 等.[J].电镀与环保,1995,15(05):18. |
| [6] | Collins J A.Failure of Materials in Mechanical Design[M].New York:Wiley,1981:369. |
| [7] | Pethica J B et al.[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1983,48(04):593. |
| [8] | 孙克宁.无电解镀镍磷非晶态合金的近边结构研究[J].高等学校化学学报,1996(02):278. |
| [9] | 范雄.金属X射线学[M].北京:机械工业出版社,1989:103. |
| [10] | Allen R M;VanderSande J B .[J].Scripta Metallurgica et Materialia,1982,16:1161. |
| [11] | Weil R;Parker K.Electroless Plating: Fundamentals and Applications[J].American Electroplaters and Surface Finishers Society,1990:111. |
| [12] | Zhang Yongzhong et al.[J].Journal of Materials Science Letters,1996,15:1364. |
| [13] | 姚枚 等.[J].金属学报,1993,29(01):A511. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%