对展现高应变速率超塑性变形行为的β-SiC晶须增强LY12铝基复合材料、β-SiC晶须增强L4纯铝基复合材料进行了差示扫描量热(DSC)分析,探讨微量液相在铝基复合材料高应变速率超塑性变形过程中的作用.研究表明:适当的微量液相是铝基复合材料获得好的高应变速率超塑性的必要条件.