研究了二维C/C(2D-C/C)复合材料在高温下层剪强度、弯曲强度和模量、热导率和线膨胀系数的变化规律.结果表明,所制得的2D-C/C复合材料的层剪强度随温度的升高变化不大、弯曲强度随测试温度的升高而增加;2 000℃的层剪强度、弯曲强度分别达到14.8 MPa和227.4 MPa,较室温分别提高了9.6%和60%.弯曲模量在1 000℃时增加到39.4 GPa,在2 000℃则下降,低于室温数值.2D-C/C复合材料的热导率、线膨胀系数在z向和x-y向都具有明显的各向异性.未石墨化2D-C/C复合材料200℃的z向热导率是4.41 W/(m·K),且随温度的升高而增加;而石墨化2D-C/C复合材料200℃的z向、x-y向热导率分别是18.02W/(m·K)和73.29W/(m·K),随温度的升高而下降.2D-C/C复合材料在z向的线膨胀系数较大,800℃以内在8×10-6/K～10×10-6/K之间;而在x-y向线膨胀系数在800℃以内都很小,基本上接近于零.
参考文献
| [1] | Kogo Y;Hatta H;Fujikura M .Mechanical properties of carbon fiber-reinforced carbon composite at elevated temperature[J].Tanso,1995,166:40-44. |
| [2] | Takehara M;Matrumoto Y et al.Interlaminar shear strength of C/C composites at elevated temperature[J].Tanso,1996,173:168-171. |
| [3] | Fukuda H;Itohiya G .The influence of thermal shock on interlaminar shearing strength of woven C/C composites[J].日本复合材料学会志(日本),1998,24(05):183-191. |
| [4] | Peebles L H;Meyer R A;Joiner J.Interfaces in carboncarbon composites;interfaces in polymer,ceramic,and metal matrix composites[M].Matsuo Ishide edited.Elsevier Science Publishing Co.Inc.,1988:1-14. |
| [5] | Buch J D .Graphite crystals-A general model for diverse carbon forms specifically C/C composites;high performance metal and ceramic matrix composites[Z].Upadhya K edited.The Minerals,Metals & Materials Society,1994. |
| [6] | 陈蔚然.碳素材料工艺基础[M].长沙:湖南大学出版社,1985:231-252. |
| [7] | 植村益次;牧广(日)主;贾丽霞;白淳岳.高性能复合材料最新技术[M].北京:中国建筑工业出版社,1989:26-31. |
| [8] | Baker C .A high temperature light weight nozzle material[R].AIAA 94-2692,1994. |
| [9] | 八田博志 .C/C复合材料的高温热物性[J].材料体系,1995,14(06):15-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%