采用六甲基二硅氮烷(HMDZ)和六甲基二硅氧烷(HMDSO)为表面改性剂,对正硅酸乙酯(TEOS)经溶胶-凝胶过程制备的凝胶进行表面改性,大幅度简化了洗涤过程,常压干燥制备了疏水SiO2气凝胶,并研究了表面改性剂对SiO2气凝胶结构和性能的影响.结果表明,所制备的疏水SiO2气凝胶有良好的疏水性能,吸附水量低于3%,与水的接触角大于130°;疏水SiO2气凝胶的密度、比表面积和孔隙率分别为150～225 kg/m3、750～900 m2/g和88%～93%,其颗粒尺寸为1～100 nm.
参考文献
| [1] | Kistler S S .Coherent expanded aerogels[J].Journal of Physical Chemistry,1932,34:52-56. |
| [2] | Young-Geun Kwon;Se-Young Choi .Ambient-dried insulation[J].Journal of Materials Science,2000,35:6075-6078. |
| [3] | Hrubesh LW. .Aerogel applications[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):335-342. |
| [4] | 吴志坚.无机气凝胶研究进展[J].材料导报,2001(11):38-40. |
| [5] | Smith DM.;Boes U.;Maskara A. .Aerogel-based thermal insulation[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):254-259. |
| [6] | 姚连增,李小毛,蔡维理,李远红,牟季美,陈志强,何国良,张立德.SiO2气凝胶的制备与表征[J].硅酸盐学报,1998(03):319-323. |
| [7] | Valerie D L;Thomas M H;Dale C T .Process of lowdensity silica gel by critical point drying or ambient drying[J].Journal of Non-Crystalline Solids,2001,283:11-17. |
| [8] | YOUNG-GEUN KWON;SE-YOUNG CHOI;EUL-SON KANG .Ambient-dried silica aerogel doped with TiO_(2) powder for thermal insulation[J].Journal of Materials Science,2000(24):6075-6079. |
| [9] | Valerie D L;Thomas M .Teeters.Process of low-density silica gel by critical point drying or ambient drying[J].Journal of Non-Crystalline Solids,2001,283:11-17. |
| [10] | 李兴华.密度·浓度测量[M].北京:中国计量出版社,1991:213. |
| [11] | Bikerman J J.Surface chemistry:theory and application[M].New York:Academic Press,1985:343. |
| [12] | Rao AV.;Kulkarni MM.;Amalnerkar DP.;Seth T. .Surface chemical modification of silica aerogels using various alkyl-alkoxy/chloro silanes[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):262-270. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%