针对AZ31镁合金,研究了在A-TIG焊中单一成分的活性剂和涂敷量对焊缝成形的影响.结果表明,与无活性剂的焊缝相比,活性剂TiO2、SiO2、Cr2O3、CdCl2和CaCl2能够有效地增加镁合金焊缝的熔深和深宽比.但涂敷有氟化物的镁合金焊缝熔深没有增加,涂敷CaF2的焊缝甚至出现开裂现象.在AZ31镁合金的焊接中,活性剂CdCl2的效果最好.
参考文献
| [1] | Howse D.;Lucas W. .Activating flux-increasing the performance and productivity of the TIG and plasma processes[J].Welding & Metal Fabrication: Welding and Joining Practice and Technology,1996(1):11-17. |
| [2] | Lucas W .Activating flux improving the performance of the TIG process[J].Welding & Metal Fabrication,2000,68(02):6-10. |
| [3] | Dunn G J;Allemand C D;Egger T W .Metal vapors in gas tungsten arcs:part.spectroscopy and monochromatic photography[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17(10):1851-1863. |
| [4] | Heiple C R;Rooper J T .Effect of selenium on GTAW fusion zone geometry[J].Welding Journal,1981,60(08):143-145. |
| [5] | 张瑞华,樊丁.低碳钢A-TIG焊活性剂的焊接性[J].焊接学报,2003(01):85-87,90. |
| [6] | 刘凤尧,杨春利,林三宝,吴林,张清涛.活性化TIG焊熔深增加机理的研究[J].金属学报,2003(06):661-665. |
| [7] | M. MARYA;G.R. EDWARDS .Chloride Contributions in Flux-Assisted GTA Welding of Magnesium Alloys[J].Welding Journal,2002(12):(291-S)-(298-S)-0. |
| [8] | 张兆栋,刘黎明,王来.镁合金活性TIG焊焊接接头组织特征分析[J].焊接学报,2004(04):55-58. |
| [9] | 吴信辉.电子束或电弧焊接镁合金之微织构与机性分析[M].台北:国立中山大学材料研究所,2003 |
| [10] | 张赋升,马铁军,李京龙,熊江涛,杨宁宁.A-TIG焊电弧的动态研究[J].电焊机,2003(12):17-19,51. |
| [11] | 朱士尧.等离子体物理基础[M].北京:科学出版社,1983:19-37. |
| [12] | 张清辉.焊接材料研制理论与技术[M].北京:冶金工业出版社,2002:7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%