通过对铼与钛合金焊接脆性的产生机理进行分析,采取增加中间层材料进行电子束焊连接的方法来克服接头脆性.根据理论分析的结论确定了中间层材料类别,制定了多组中间层配方成分,通过焊接试验与相关测试,最终实现了对接头脆性相的有效控制.
参考文献
| [1] | 陈健.燃烧室新材料在卫星双组元低推力发动机上的应用[J].航天控制,2001(04):8-14,34. |
| [2] | 许菱,许孙曲.高熔点金属的新应用[J].稀有金属快报,2000(11):15-16. |
| [3] | 李曙光.难熔金属应用几例[J].航天工艺,1996(03):40. |
| [4] | 胡德昌;胡滨.航天航空用新材料--难熔金属及其合金[J].航天工艺,1996(03):34-40. |
| [5] | Stechman C;Woll P;Fuller R et al.A high performance liquid rocket engine for satellite main propulsion[AIAA,20003161][R]. |
| [6] | Reed B D;Biaglow J A .Rhenium mechanical properties and joining technology.[NASA Technical Memorandum 107317,AIAA 96 2598][R]. |
| [7] | John O M;Dan J T;Gary K L .Directed light fabrication of rhenium components:materials science and technology division[NM 87545][R].,1987. |
| [8] | Donald J;Butler S.Joining and fabricating rhenium using explosive metal working techniques[M].Proiect Engineer,WA 98382,1998 |
| [9] | 葛志明.钛的二元素相图[M].北京:国防工业出版社,1977 |
| [10] | Villars P;Prince A;Okamoto H.Handbook of ternary alloy phase diagrams[M].Materials Park:ASM International,1995 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%