研究了Nb-15Ti-11Al和Nb-15Ti-11Al-10Si两种多元铌合金在1 100和1 300℃高温下的氧化行为,建立了合金高温氧化动力学模型.结果表明:粉末冶金方法制备的铌合金微观组织细小,大大降低了氧的短路扩散;合金中的钛降低了氧在基体中的固溶度并降低了氧的扩散速率;合金中的硅在高温时形成熔融态的SiO2可有效地抑制Nb2O5,的生长,从而保证了氧化膜表面均匀平整.
参考文献
| [1] | Viars P R.The impact of IHPTET on the engine:aircraft system[Report A1AA-892137][A].Seattle,Washington,1988 |
| [2] | Dollar A;Dymek S.Microstructure and high temperature mechanical properities of mechanically alloyed Nb3Al-based eterials[J].Intermetallics,2003(11):341. |
| [3] | Yonosuke Murayama;Shuji Hanada .High temperature strength, fracture toughness and oxidation resistance of Nb-Si-Al-Ti multiphase alloys[J].Science and technology of advanced materials,2002(2):145-156. |
| [4] | Sikka V K;Aloria E .Characteristics of a mu]ticomponent Nb-Ti-Al alloy via industrial-scale practice[J].Materials Science and Engineering,1997,A239-240:745. |
| [5] | Perkins R A;Meier G H.The oxidation behavior and protection of niobium[J].JOM-Journal of the Minerals Metals and Materials Society,1990(08):17. |
| [6] | 牛焱 等.Fe-Nb合金在600～800℃、0.1 MPa纯氧中的氧化[J].金属学报,1996,32(03):294. |
| [7] | 牛炎;Gesmundo F C 等.两种Co-Nb合金在600℃～800℃、1大气压纯氧中的氧化[J].中国腐蚀与防护学报,1996,16(04):247. |
| [8] | 牛焱.在600-800℃低氧压下Co-Nb合金的氧化[J].腐蚀科学与防护技术,1995(02):130. |
| [9] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:79. |
| [10] | Daniel Monceau et al.Determination of parabolic rate constants from a local analysis of mass-gain curves[J].Oxidation of Metals,1998,50(5-6):447. |
| [11] | 唐仁正.物理冶金基础[M].北京:冶金工业出版社,1997:38. |
| [12] | 于振涛,李东,吴玮璐,邱绍宇,王兴旺.钛合金在高温高压过热蒸汽中的腐蚀机理研究[J].核动力工程,2004(05):452-456,480. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%