为改进纤维增强氰酸酯树脂基复合材料的制备工艺,研制了一种适用热熔法制备预浸料的氰酸酯树脂体系.以旋转黏度计确定了适用热熔法浸渍纤维的树脂黏度为1.5 Pa·s/80℃、最佳加工温度为(90±2)℃、工艺适用期为2 h.利用DSC及哈克流变仪确定了树脂的固化工艺、纤维增强树脂基复合材料的制备工艺等.结果表明此树脂体系具有良好的热熔加工性能,适宜的工艺适用期,树脂体系在-10℃下贮存6个月后,树脂黏度基本保持不变,应用热熔浸渍法制备的M40J碳纤维/氰酸酯复合材料,具有优异的力学性能,拉伸强度和模量分别为2 037 MPa和226 GPa,弯曲强度和模量分别为1 580 MPa和217 GPa.
参考文献
| [1] | Hanerton I;Herman H;Rees K T et al.Water uptake efects in resins based on alkenyl modified cyanate ester-bismaleimide blends[J].Polymer International,2001,50:475-483. |
| [2] | Srinivasan S A;Mcgrrath J E .Amorphous phenolphthalein-based poly(arylene ether)modified cyanate ester networks:1.Efeet of molecular weight and backbone chemistry on morphology and toughenability[J].POLYMER,1998,39(12):2 415-2 427. |
| [3] | Liang GZ.;Zhang MX. .Enhancement of processability of cyanate ester resin via copolymerization with epoxy resin[J].Journal of Applied Polymer Science,2002(11):2377-2381. |
| [4] | Isabel H;Clara M G;Marcos D R et al.Cure monitoring of catalysed cyanate ester resins[J].Polymer International,2000,49(07):735-742. |
| [5] | 任鹏刚,梁国正,杨洁颖,宫兆合,卢婷利.环氧改性氰酸酯复合材料工艺性研究[J].宇航材料工艺,2003(05):26-30,34. |
| [6] | 任鹏刚,梁国正,顾嫒娟.卫星用M40/BADCy复合材料研究[J].材料科学与工艺,2005(06):582-585. |
| [7] | 杨洁颖,梁国正,任鹏刚,王结良,房红强,周文胜.改性氰酸酯树脂基复合材料的研究[J].功能材料,2004(05):582-584. |
| [8] | 任鹏刚,梁国正,杨洁颖,王结良,卢婷利.高性能M40J/BADCy复合材料的研究[J].航空学报,2004(04):411-415. |
| [9] | Coggwell F N;Hezzell;Williams P J .Fibre-reinforced composites and methods for producing such composites[P].EPO0056703,1982. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%