综述了消除复合材料界面裂纹应力奇异性及求解界面模态混合度的主要方法,分析讨论了各个方法的优缺点.通过分析讨论发现:模态混合度表征界面力学性能可以准确地描述界面裂纹尖端处各应变能释放率分量的振荡特性;求解与裂纹扩展长度无关的各应变能释放率分量及模态混合度是研究复合材料界面裂纹问题的难点;采用混合模态界面力学性能试验方法验证基于正则化长度等求解模态混合度方法的有效性,进而准确预测复合材料分层的发生及扩展是今后研究复合材料界面力学问题的发展方向.
参考文献
| [1] | Miller A G;Lowell D T;Seferis J C .The evolution of an aerospace material:Influence of design manufacturing and in-service performance[J].Composite Structures,1994,27:193-206. |
| [2] | B. Fiedler;M. Hojo;S. Ochiai .The influence of thermal residual stresses on the transverse strength of CFRP using FEM[J].Composites, Part A. Applied science and manufacturing,2002(10):1323-1326. |
| [3] | Williams M L .The stresses around a fault or crock in dissimilar media[J].Bulletins of the Seismological Society of America,1959,49(02):199-204. |
| [4] | Rice J R;Sih G C .Plane problems of cracks in dissimilar media[J].Journal of Applied Mechanics,1965,32:418-423. |
| [5] | Comninou M .An overview of interface cracks[J].Engineering Fracture Mechanics,1990,37:197-208. |
| [6] | O'Brien T K.Towards a damage tolerance philosophy for composite materials and structures[A].,1990:7-33. |
| [7] | Chai H.Experimental evaluation of mixed-mode fracture in adhesive bonds[J].Experimental Mechanics,1992:296-303. |
| [8] | Majumdar B S;Miracle D B .Interface measurements and applications in fiber-reinforced[J].MMCs Key Eng Mater,1996,116/117:153-172. |
| [9] | Kalton A F;Howward S J;Janczk-rusch J et al.Measurement of interfacial fracture energy by single fiber push out testing and its application to the titanium silicon carbide system[J].Acta Materialia,1998,9:3175-3189. |
| [10] | Antonio Miravete;Miguel A Jimenez .Application of the finite element method to prediction of onset of delamination growth[J].Applied Mechanics Reviews: An Assessment of the World Literature in Engineering Sciences,2002(2):89-106. |
| [11] | Evans A G;Ruhle M;Dalgleish B J;Charalambides PG .Tae fracture energy of bimaterial interfaces[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1990,126:53-64. |
| [12] | Wang J S;Suo Z .Experimental determination of interfacial toughness curves using brazil-nut sandwiches[J].Acta Materialia,1990,38(07):1279-1290. |
| [13] | O'Dowd N P;Shih C F;Stout M G .Test geometries for measuring interfacial fracture toughness[J].Int J Solids,1992,29(05):571-589. |
| [14] | Yuuki R;Liu J Q;Xu J Q et al.Mixed mode fracture criteria for an interface crack[J].Engineering Fracture Mechanics,1994,47(03):367-377. |
| [15] | Kardomateas G A .The initial postbuekling and growth behavior of internal delaminafions in composite plates[J].Journal of Applied Mechanics,Transactions of the ASME,1993,60:903-910. |
| [16] | Kardomateas G A;Pelegri A A;Malik B .Growth of internsl delaminafions under cycle compression in composite plates[J].Journal of the Mechanics and Physics of Solids,1995,43(06):847-868. |
| [17] | Blanco N;Garnstedt EK;Asp LE;Costa J .Mixed-mode delamination growth in carbon-fibre composite laminates under cyclic loading[J].International Journal of Solids and Structures,2004(15):4219-4235. |
| [18] | S. Bennati;P.S. Valvo .Delamination growth in composite plates under compressive fatigue loads[J].Composites science and technology,2006(2):248-254. |
| [19] | BARRY D.DAVIDSON;SIMON J.GHARIBIAN .Evaluation of energy release rate-based approaches for predicting delamination growth in laminated composites[J].International Journal of Fracture,2000(4):343-365. |
| [20] | Beuth J L .Separation of crack extension modes in orthotropic delamination models[J].International Journal of Fracture,1996,77:305-321. |
| [21] | Agrawal A;Karlsson A M .Obtaining mode mixity for a biomatefial interface crack using the virtual crack closure technique[J].International Journal of Fracture,2006,141:75-98. |
| [22] | Te Tay .Characterization and analysis of delamination fracture in composites: An overview of developments from 1990 to 2001[J].Applied Mechanics Reviews: An Assessment of the World Literature in Engineering Sciences,2003(1):1-32. |
| [23] | Rice J R .Elastic fracture mechanics concepts for interfacial cracks[J].Journal of Applied Mechanics,Transactions of the ASME,1988,55:98-103. |
| [24] | Erdogan A H .Stress distribution in bonded dissimilar materials with cracks[J].Journal of Applied Mechanics,Transactions of the ASME,1965,32:403-410. |
| [25] | Atkinson C .On stress singularities and interfaces in linear elastic fracture mechanics[J].International Journal of Fracture,1977,13:807-820. |
| [26] | Raju I S;Crews J H;Aminpour M A .Convergence of strain energy release rate components for edge-deluminated compesite laminates[J].Engineering Fracture Mechanics,1988,30(03):383-396. |
| [27] | Hutchinson J W;Suo Z .Mixed mode cracking in layered materials[J].Advances in Applied Mechanics,1992,29:63-191. |
| [28] | Davidson B D.Prediction of energy release rate for edge delumination using a crack tip element[A].,1995:155-175. |
| [29] | Davidson B D .Energy release rate determination for edge delamination under combined in-plane,bending and hygrothermal loading.Part I -delamination at a single interface[J].Journal of Composite Materials,1994,28:1009-1031. |
| [30] | He M Y;Hutchinson J W .Kinking of a crack out of an interface[J].Journal of Applied Mechanics,Transactions of the ASME,1989,56:270-278. |
| [31] | Suo Z;Hutchinson J W .Sandwich test specimens for measuring interface crack toughness[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1989,107:135-143. |
| [32] | Davidson B D;Hu H;Schapery R A .An analytical crack tip element for layered elastic structures[J].Journal of Applied Mechanics,Transactions of the ASME,1995,62(06):243-253. |
| [33] | Davidson B D;Hu H .Effect of interlayer modulus on fracture mode ratio for interleaved composite laminates[J].Engineering Fracture Mechanics,1995,52(02):243-253. |
| [34] | Sun C T;Manoharan M G .Strain energy release rates of an interfacial crack between two orthotropic solids[J].J Compo Mater,1989,23:460-478. |
| [35] | Hwu C;Hu J S .Stress intensity factors and energy release rates of delaminatious in composite laminates[J].Engineering Fracture Mechanics,1992,42(06):977-988. |
| [36] | Kuflu Z;Chang F K .Composite panels containing multiple through-the-width delaminations and subjected to compres sion Part Ⅰ:analysis[J].Compos Strnct,1995,31:273-296. |
| [37] | S. C. Pradhan;T. E. Tay .Three-dimensional finite element modelling of delamination growth in notched composite laminates under compression loading[J].Engineering Fracture Mechanics,1998(2):157-171. |
| [38] | Martin R H.Incorporating interlarninar fracture mechanics into design[M].London,1998:83-92. |
| [39] | Rybicki E F;Kannincn M F .A finite element calculation of stress intensity factors by a modified crack closure integral[J].Engineering Fracture Mechanics,1977,9:931-938. |
| [40] | A. Agrawal;A. M. Karlsson .On the Reference Length and Mode Mixity for a Bimaterial Interface[J].Journal of engineering materials and technology,2007(4):580-587. |
| [41] | Toya M .On mode I and mode II energy release rates of an interface crack[J].International Journal of Fracture,1992,56:345-352. |
| [42] | Sun C T;Jih C J .On strain energy release rates for interracial cracks in bi-material media[J].Engineering Fracture Mechanics,1987,28(01):13-20. |
| [43] | Suo Z .Singularities,interfaces and cracks in dissimilar anisotropic media[J].Proe R SOc London SOr A,1990,427:331-358. |
| [44] | Qian W.;Sun CT. .Methods for calculating stress intensity factors for interfacial cracks between two orthotropic solids[J].International Journal of Solids and Structures,1998(25):3317-3330. |
| [45] | Reeder J R;Crews J H.Non-linear analysis and redesign of the mixed-mode bending delamination test[M].NASA Technical Memorandum,1991 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%