采用不同厚度的电镀镍作为中间层,在900℃、4 h和150 MPa压力的热等静压条件下,使用TCA预合金粉末和GCr15轴承钢制备了钛钢扩散焊接头.利用光学显微镜、扫描电镜、XRD和机械拉伸对接头进行了测试和分析.结果表明:当没有添加中间层时,接头的强度达到了564 MPa;当添加了中间层且中间层的厚度为150μm时,接头的强度最高,为502 MPa.中间层过厚或者过薄,都会导致接头强度的下降.
参考文献
[1] | 邹茉莲.钛合金TC4与1Cr18Ni9Ti不锈钢的扩散焊工艺探索[J].北京航空航天大学学报,1995(03):45. |
[2] | 宋敏霞,赵熹华,郭伟,冯吉才.钛合金与其它金属材料扩散连接研究现状与发展[J].焊接,2005(01):5-7. |
[3] | 孙荣禄;李慕勤;张九海 等.中间过渡金属对钛合金与不锈钢扩散焊接头强度的影响[J].焊接学报,1996,17(04):212-218. |
[4] | Kundu S S C .Interfacial microstructure and mechanical properties of diffusion-bonded titanium-stainless steel joints using a nickel interlayer[J].Materials Science and Engineering A,2007,425:107-113. |
[5] | Lang Zebao;Wang Liang;Zhang Xuhu .HIP diffusion bonding of P/M titanium alloy Ti-6Al-4V and stainless steel 1Cr18Ni9Ti[J].Transactions of Nonferrous Metals Society of China,2007,17:79-83. |
[6] | Kundu S;Chatterjee S;Olson D.Effects of intermetallic phases on the bond strength of diffusion-bonded joints between Titanium and 304 stainless steel using nickel interlay[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2007(38A):2053-2060. |
[7] | He P;Zhang J;Zhou R et al.Diffusion bonding technology of a titanium alloy to a stainless steel web with an Ni interkayer[J].Materials Characterization,1999,43:287-292. |
[8] | Wang Liang;Lang Zebao;Shi Hongpei .Properties and forming process of prealloyed powder metallurgy Ti-6Al-4V alloy[J].Transactions of Nonferrous Metals Society of China,2007,17(z1):639-643. |
[9] | Froes F H;Eylon D.Titanium powder metallurgy-a review[A].Pennsylvania:The Metallurgical Society of AIME,1984:1-20. |
[10] | Sheinker A A;Chananie G R;Bohlen J W .Evaluation and application of prealloyed titanium P/M parts for airframe structures[J].International Journal of Powder Metallurgy,1987,23(03):171-179. |
[11] | Delo D P;Piehler H R .Early stage consolidation mechanisms during hot isostatie pressing of Ti-6Al-4V powder compacts[J].Acta Materials,1999,47(09):2841-2852. |
[12] | 《中国航空材料手册》编辑委员会.[M].北京:中国标准出版社,2001:505. |
[13] | Kundu S;Chatterjee S.Characterization of diffusion bonded joint between titanium and 304 stainless steel using a Ni interlay[J].Materials Characterization,2007 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%