研究了高温真空环境下多孔(气孔率>50%)氯化硅陶瓷的弯曲强度,并进行了初步分析.结果表明,多孔氮化硅陶瓷在真空中的高温强度随温度上升而降低,由于没有氧化作用,晶界玻璃相在高温下的软化成为影响其强度的主要因素.
High temperature flexural strength of porous silicon nitride ceramics ( no less than 50% porosity) under vacuum conditions was studied, and the phases after high temperature strength testing was analysed also. The results show that the flexural strength of porous silicon nitride ceramics is negatively related with temperature under vacuum condition. The softening of glassy phase on grain boundary under high temperature is the main factor influencing the strength decrease.
参考文献
| [1] | Riley F.L.;, .Silicon Nitride and Related Materials[J].Journal of the American Ceramic Society,2000(2):245-265. |
| [2] | Jian-Feng Yang;Tatsuki Ohji;Shuzo Kanzaki .Microstructure and Mechanical Properties of Silicon Nitride Ceramics with Controlled Porosity[J].Journal of the American Ceramic Society,2002(6):1512-1516. |
| [3] | 薛友祥;王耀明.多孔陶瓷材料引领国内过滤技术发展[J].中国粉体技术,2008(05):58-61. |
| [4] | Mori H.;Yoshimura N.;Hotta T.;Ayama K.;Tsubaki JI.;Mase S. .Fabrication of supported Si3N4 membranes using the pyrolysis of liquid polysilazane precursor[J].Journal of Membrane Science,1998(1):23-33. |
| [5] | 王红洁,王永兰,金志浩.不同介质中Si3N4陶瓷的静疲劳与循环疲劳[J].稀有金属材料与工程,2003(08):639-642. |
| [6] | 罗学涛;张长瑞;周新贵 .Y-La-Si_3N_4陶瓷的高温力学性能及氧化特征[J].国防科技参考,1997,18(04):62-64. |
| [7] | Zeng Jianren;Tanaka I;Miyamoto Y et al.High-temperature strength and cavitation threshold of silicon nitride-siliea ceramics[J].Journal of the American Ceramic Society,1992,75(01):195-200. |
| [8] | Yokoyama K.;Wada S. .Solid-Gas Reaction during Sintering of Si_3N_4 Ceramics (Part 5)-Mass Change of Si_3N_4 Ceramics during Sintering under N_2 Gas Flow in a Non-Carbon-Element Furnace-[J].日本セラミックス协会学术论文志,2000(1259):627-632. |
| [9] | 王红洁,王永兰,金志浩.Si3N4陶瓷的显微结构与阻力行为[J].西安交通大学学报,2000(12):59-62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%