制备了苯并噁嗪树脂/BMI/环氧树脂三元体系,采用动态DSC分析了三元体系的固化反应过程.并用Kissinger 和Ozawa 方法分别求得三元体系的反应活化能为89.5 kJ/mol.由Crane 理论计算得到该体系的固化反应级数n=0.93级反应;根据计算的动力学参数,建立了三元体系的固化动力学模型.利用所建立的固化动力学模型分别预测了等温和动态条件下,三元体系的固化反应特性.得到了三元体系的固化工艺为 180℃/1 h+200℃/2 h+230℃/2 h,后处理工艺为250℃/2 h.
参考文献
| [1] | Jyongsik Jang;Hojung Yang .Toughness improvement of carbon-fibre/polybenzoxazine composites by rubber modification[J].Composites science and technology,2000(3):457-463. |
| [2] | Ishida H.;Allen DJ. .MECHANICAL CHARACTERIZATION OF COPOLYMERS BASED ON BENZOXAZINE AND EPOXY[J].Polymer: The International Journal for the Science and Technology of Polymers,1996(20):4487-4495. |
| [3] | 王劲,顾宜,谢美丽.苯并噁嗪-环氧树脂基玻璃布层压板的研究[J].塑料工业,2001(05):6-8. |
| [4] | Takeichi T;Guo Y;Rimdusit S .Performance improvement of polybenzoxazine by alloying with polyimide: effect of preparation method on the properties[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(13):4909-4916. |
| [5] | Ishida Hatsuo;Ohha Sharon .Synthesis characterization of maleimide and nitrile-fundtionalized benzoxazine[J].Polymer,2005,46:5588-5595. |
| [6] | 赵庆来,曾科,韩勇,唐艳,周柯,唐文睿,杨刚.含马来酰亚胺和烯丙基醚的苯并（口恶）嗪的合成与性能[J].高分子材料科学与工程,2007(03):51-54. |
| [7] | 李玲,陈剑楠.改性BMI/苯并噁嗪树脂的固化反应及其动力学研究[J].中国胶粘剂,2008(10):23-26. |
| [8] | Xing Hatsuo Ishida .Phenolic material via-ring opening polymerization:systhesis and characterization of bisphenol-A based benzoxazines and their polymers[J].Polymer Science Part A:polym Chem,1994,32(06):1121-1129. |
| [9] | 李玲,梁国正,蓝立文,范儆,周毅.烯丙基酚氧树脂改性BMI的研究[J].高分子材料科学与工程,1999(02):116-119. |
| [10] | 于伯龄.实用热分析技术[M].北京:纺织工业出版社,1990 |
| [11] | 王焱,王先胜,陈海生.树枝形大分子/环氧树脂体系固化反应动力学研究[J].高分子通报,2006(11):40-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%