以碱为催化剂,通过联苯型酚醛树脂与4-硝基邻苯二甲腈之间的亲核取代反应,制备了邻苯二甲腈基联苯型酚醛树脂(PBN).流变性能测试结果表明,PBN树脂在180 ~ 300℃,黏度<400 mPa·s,表明该树脂具有优良的加工性能.DSC测试结果表明,PBN树脂的固化温度为280~450℃,固化反应峰值温度为377℃,固化放热约为187 J/g.该树脂表现出优良的耐热性,其储能模量起始下降温度高于450℃,Td5约为529℃,氮气氛围、900℃残碳率约为78%.
参考文献
[1] | 朱其仁,李锦春,王丽娟,杜新宇,谭伟,吴娟.苯酚-亚联苯型酚醛树脂的合成与表征[J].化工学报,2009(04):1052-1056. |
[2] | Dawn D.Dominguez;Teddy M.Keller .Properties of phthalonitrile monomer blends and thermosetting phthalonitrile copolymers[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(26):91-97. |
[3] | 郑劲东.舰船用新型耐高温阻燃结构材料--聚邻苯二甲腈复合材料[J].材料导报,2002(10):63-66. |
[4] | Yan Y H;Shi X M;Liu J G.Thermosetting resin system based on novolak and bismaleimide for resin-transfer molding[J].Journal of Applied Polymer Science,2002(83):1651-1657. |
[5] | SASTRI SATYA B.;KELLER TEDDY M. .Phthalonitrile Polymers: Cure Behavior and Properties[J].Journal of Polymer Science, Part A. Polymer Chemistry,1999(6):2105-2111. |
[6] | Sastri SB.;Keller TM. .Phthalonitrile cure reaction with aromatic diamines[J].Journal of Polymer Science, Part A. Polymer Chemistry,1998(11):1885-1890. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%