为提高高模量碳纤维复合材料的力学性能,研究改性氰酸酯、5228、4211与碳纤维结合面结合性能.用SEM、AFM、微脱粘仪、万能力学试验机等仪器设备,观察了碳纤维表面微观形貌、树脂基体与碳纤维结合面微观粘接情况,并对复合材料的宏观力学性能进行分析研究.结果表明,高模量碳纤维随着模量的提高,袁层的缺陷与沟槽减少、表面活性降低,与树脂的结合面粘接强度减弱；改性氰酸酯与纤维的结合面粘接性能较好、5228次之、4211较差；树脂与纤维结合面粘接强度大的,其复合材料的力学性能好.
参考文献
| [1] | Mallon J J;Uht J C;Hemminger C S.Surface analyses of composites exposed to the space of spacecraft on the long duration exposure facility satellite[J].Journal of Spacecraft and Roekets,1993(30):495. |
| [2] | Felbeck DK. .TOUGHENED GRAPHITE-EPOXY COMPOSITES EXPOSED IN NEAR-EARTH ORBIT FOR 5.8 YEARS[J].Journal of spacecraft and rockets,1995(2):317-323. |
| [3] | 赵渠森.先进复合材料手册[M].北京:机械工业出版社,2003 |
| [4] | Lakshmi MS.;Reddy BSR. .Synthesis and characterization of new epoxy and cyanate ester resins[J].European Polymer Journal,2002(4):795-801. |
| [5] | Kim BS. .EFFECT OF CYANATE ESTER ON THE CURE BEHAVIOR AND THERMAL STABILITY OF EPOXY RESIN[J].Journal of Applied Polymer Science,1997(1):85-90. |
| [6] | 陈平,程子霞,金镇镐,雷清泉.环氧树脂与氰酸酯共固化产物性能的研究[J].高分子学报,2001(02):238-240. |
| [7] | 宫顼;董艺;肖少伯.改性氰酸酯树脂的应用研究[A].,2010 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%