为了提高蜂窝夹层结构的耐热性和高温力学性能,采用石英灯和力学性能测试的方法进行了相关性能测试.弯曲性能测试结果表明,UT500/KH370蜂窝夹层面板的弯曲强度400℃保持率为58％,弯曲模量保持率为85％,层间剪切强度保持率为57％；石英灯静态隔热试验结果表明,冷壁热流为300 kW/m2的条件下,高度为29mm的蜂窝夹层板的背温为320℃；冷壁热流为168 kW/m2的条件下,背温为296℃.
参考文献
| [1] | Kathy C.Chuang;Cheryl L.Bowman;Thomas K.Tsotsis;Cory P.Arendt .6F-Polyimides with Phenylethynyl Endcap for 315-370deg C Applications[J].High performance polymers,2003(4):459-472. |
| [2] | Takekoshi T;Terry J M .High-temperature thermoset polyimides containing disubstituted acetylene end groups[J].Polymer,1994,35(22):4874-4880. |
| [3] | R. A. Gray;L. R. McGrath .The Development of High-Temperature Polyimides for Resin Transfer Molding[J].SAMPE Journal,2004(6):23-31. |
| [4] | Connell J W;Smith J G Jr et al.High temperature transfer molding resins:preliminary composite properties of PETI-375[J].SAMPE Symposium,2004,49(01) |
| [5] | 陈建升,左红军,高群峰,何冠君,范琳,杨士勇.苯乙炔基封端PMR型聚酰亚胺树脂的制备与性能研究[J].航空材料学报,2007(05):66-70. |
| [6] | 孟祥胜,杨慧丽,范卫锋,王震.高韧性异构聚酰亚胺树脂及其复合材料[J].宇航材料工艺,2009(03):53-57. |
| [7] | 曲希明,冀棉,赵伟栋,范琳,杨士勇.耐371℃ PMR型含异构联苯结构的聚酰亚胺树脂及复合材料[J].宇航材料工艺,2009(02):50-53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%