针对C/C复合材料脆性问题,对密度为1.60 g/cm3的碳布叠层针刺C/C复合材料进行了1800、2 000、2 200和2 500℃的高温处理,研究了不同热处理温度对C/C复合材料微晶结构、力学和抗热震等性能的影响.结果表明,高温处理使针刺C/C复合材料的层间剪切和面内拉伸强度出现不同程度的降低,但材料的断裂伸长率和抗热震性能得到大幅度提高.其中,1 800℃高温处理后的C/C复合材料具有优异的力学和抗热震性能.
参考文献
| [1] | Fitzer E .The future of carbon-carbon composites[J].CARBO,1987,25(02):163. |
| [2] | Heshmat A .The effect of intermediate graphitization on the mechanical and fracture behavior of 2D C/C composites[J].CARBO,1993,31(07):1121-1129. |
| [3] | 马伯信.碳/碳复合材料工艺基础[M].航天四院,2002 |
| [4] | 陈蔚然.石墨化过程的热力学和动力学分析[J].碳素,1982(01):11-16. |
| [5] | 苏波.复合材料学[M].长沙:国防科技大学出版社,1985 |
| [6] | 陈腾飞,龚伟平,张红波,肖鹏,熊翔.高温热处理对光滑层热解炭裂纹形成的影响[J].粉末冶金材料科学与工程,2006(04):210-213. |
| [7] | Takehara M;Matrumoto Y;kingetsu T .Interlaminar shear strength of C/C composites at elevated temperature[J].Tanso,1996,173:168-171. |
| [8] | Kazuhiro Fujita;Hiroyuki Sakai .Inflence of heat treatment temperature on interfacial shear strength of C/C composites[J].part A:Applied Science and Manufacuturing,1999,30:497-501. |
| [9] | 刘畅,魏永良,崔红,苏君明,成会明,周本濂.炭纤维增强炭基复合材料的界面[J].炭素技术,1999(03):28-32. |
| [10] | Buresova M;Cerny M.Relation between fiber volume fraction and mechanical properties of C-C-composites.Extended Abstracts and programme[A].,1998:491-492. |
| [11] | Zaldivar R J;Rellick G S;Yang J M .Processing effects on the mechanical behaviour of polyarylacetylene derived carbon-carbon composites[J].SAMPE Journal,1991,27(05):29-36. |
| [12] | 王兴业.纤维增强陶瓷基复合材料的制备、界面与性能表征[M].北京:北京大学出版社,1998 |
| [13] | Rand B;Appleyad S P.Carbon-carbon composites:the role of fiber-matrix interaction[A].Strasbourg,France,1998:1. |
| [14] | Zaldivar R J;Rellick G S .Some observation on stress graphitization in carbon-carbon composites[J].CARBO,1991,29(08):1155-1163. |
| [15] | 王明存;苏君明;王俊 .PAN基碳纤维无应力高温热处理[J].固体火箭发动机,1997,2:8-10. |
| [16] | Wan E Y .Solid rocket nozzle design summary AIAA 68-655[R]. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%