通过盐雾腐蚀实验并结合SEM和XRD分析,研究了稀土元素对锻造态ZK60镁合金腐蚀行为的影响.结果表明,ZK60合金耐蚀性较差,而在ZK60中添Gd、Y后的合金,其耐蚀性明显提高.腐蚀时间相同时,两种合金的微观腐蚀形貌不相同,ZK60合金腐蚀坑的形成时间较早(14 d),而添加Gd、Y后的ZK60合金腐蚀坑的形成时间较晚(21 d),添加Gd、Y后ZK60合金的腐蚀产物相对致密.两种镁合金的腐蚀产物均为Mg(OH)2,Mg(OH)2腐蚀产物膜极易发生开裂,形成网块状的腐蚀产物膜.腐蚀产物膜的进一步生长、开裂和脱落,加速了材料的腐蚀流失.
参考文献
[1] | ASM International.Magnesium and Magnesium Alloy[M].Ohio:Metal Park,1999:1-130. |
[2] | Polmear I J .Magnesium alloys and applications[J].Materials Science and Technology,1994,10:1-16. |
[3] | Kamado Nakatsugawa S;Kojima Y;Ninomiya R.[A].Manchester,1996:687. |
[4] | Chang Jianwei;Fu Penghuai;Guo Xingwu et al.The effects of heat treatment and zirconium on the corrosion behaviour of Mg-3Nd-0.2Zn-0 4Zr(wt%) alloy[J].Corrosion Science,2007,49:2612-2627. |
[5] | Jianwei Chang;Xingwu Guo;Shangming He;Penghuai Fu;Liming Peng;Wenjiang Ding .Investigation of the corrosion for Mg-xGd-3Y-0.4Zr (x = 6,8,10,12 wt%) alloys in a peak-aged condition[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(1):166-177. |
[6] | Xing-Wu Guo;Jian-Wei Chang;Shang-Ming He;Wen-Jiang Ding;Xishu Wang .Investigation of corrosion behaviors of Mg-6Gd-3Y-0.4Zr alloy in NaCl aqueous solutions[J].Electrochimica Acta,2007(7):2570-2579. |
[7] | 余琨,黎文献,王日初.热处理工艺对挤压变形ZK60镁合金组织与力学性能的影响[J].中国有色金属学报,2007(02):188-192. |
[8] | 丁文江,向亚贞,常建卫,彭颖红.Mg-Al系和Mg-RE系合金在NaCl溶液中的腐蚀电化学行为[J].中国有色金属学报,2009(10):1713-1719. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%