通过硬度、拉伸性能测试和金相组织观察,研究了不同退火温度对含和不合Sc的Al-Mg合金组织和性能的影响.结果表明:添加Sc明显提高了Al-Mg合金的强度,抑制了合金形变组织的再结晶,高温退火后1570合金中仍弥散分布的Al3( Sc,Zr)粒子质点造成其较高的再结晶温度及拉伸性能.
参考文献
| [1] | 柏振海,罗兵辉,谭敦强.Al-Mg-（Sc）合金退火组织和性能[J].中南工业大学学报(自然科学版),2002(06):600-603. |
| [2] | 刘可群.第二届全国铝锂合金研讨会论文集[M].长沙:中南工业大学出版社,1993:265. |
| [3] | Kumar K S;Brown S A;Pickens J R .Microstructureevolut ion duringaging of an Al-Li-Mg-Ag-Zr alloys[J].Acta Materials,1996,44(05):1899-1915. |
| [4] | Lavernia E J;Grant N J .Review aluminum-lithium alloys[J].Journal of Materials Science,1987,22:1521-1529. |
| [5] | Drit A M;Krimova T V et al.Aluminum-lithium alloys for aerospace[J].Advance Mater Process,1998,6:48-51. |
| [6] | Frudl Jander I N;Ka Blov E N;KoloBnev N I et al.Aluminum-base alloy and article made of it[P].Ru SSiaPatent,2163940,1999. |
| [7] | Joh Chung-Hyung;Yamada Kazuhiro;Miura Yasuhiro .Effect of Sc-addition on coarsening behavior of Al3 Li precipitates in Al-Li alloys[J].Materials Transactions,1998,5(40):439-443. |
| [8] | Milman Y V;LotsKo D V;SirKo O I .Sc effect of improving mechanical properties in aluminum alloys[J].Materials Science Forum,2000,331(37):1107-1112. |
| [9] | TAN Cheng-yu,ZHENG Zi-qiao,XIA Chang-qing.The Aging Feature of Al-Li-Cu-Mg-Zr Alloy Containing Sc[J].中南工业大学学报,2000(02):65. |
| [10] | 夏德顺.含钪的铝和铝锂合金[J].航天工艺,1999(02):37-42. |
| [11] | 杨志强,尹志民.俄罗斯铝-钪合金的研究与开发[J].轻合金加工技术,2003(11):34-36,40. |
| [12] | 李力,姜锋,李汉广.新世纪钪的应用开发和科技发展前景[J].稀有金属与硬质合金,2002(03):38-41. |
| [13] | 张永红 .Al-Mg-Sc-Zr合金再结晶行为的研究[J].合金与热处理,2001,24:42-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%