以4-苯乙炔基苯偶酰(PEBZ)作为封端剂,以芳香族四酮,9,9-双(4-苯偶酰氧基苯基)芴和芳香族四胺,3,3’,4,4 '-四氨基联苯(BPTA)作为单体,设计并合成了一系列苯乙炔基封端聚苯基喹恶啉(PEPPQ)树脂(PPQ-1～PPQ-4).设计分子量分别为2 500( PPQ-1)、5 000(PPQ-2)、10 000(PPQ -3)以及20 000(PPQ-4).流变分析表明,PPQ-1与PPQ -2具有良好的加工性能,350℃左右的最低黏度分别为21和568 Pa·s.通过热模压工艺制备了PPQ-1和PPQ -2固化样件,Tg分别为338和325℃.固化物具有优良的耐热稳定性,氮气中以10℃/min升温,5％失重温度均在550℃以上,750℃时的残重在60％以上.PPQ -2固化物表现出了良好的力学性能,拉伸与弯曲强度分别为88和155 MPa,断裂伸长率达到7.6％.
参考文献
| [1] | Hergenrother P M;Levine H H .Phenyl-substituted polyquinoxalines[J].Journal Polymer Science:Part A-1,1967,5:1453-1466. |
| [2] | Rabilloud G.High-performance polymers.2.polyquinoxalines and polyimides[M].Editions Technip:Paris,1999:1-32. |
| [3] | Fengcai Lu .Some Heterocyclic Polymers and Polysiloxanes[J].Journal of Macromolecular Science.Reviews in Macromolecular Chemistry and Physics,1998(2):143-205. |
| [4] | Paul M. Hergenrother .The Use, Design, Synthesis, and Properties of High Performance/High Temperature Polymers: an Overview[J].High performance polymers,2003(1):3-45. |
| [5] | J. W. Connell;J. G. Smith Jr.;P. M. Hergenrother .Oligomers and Polymers Containing Phenylethynyl Groups[J].Journal of Macromolecular Science.Reviews in Macromolecular Chemistry and Physics,2000(2/3):207-230. |
| [6] | 李诚,刘金刚,杨士勇.聚苯基喹噁啉的研究与应用进展[J].高分子通报,2010(02):1-10. |
| [7] | Beland S.High Performance Thermoplastic resins and their composites[M].Noyes:New Jersey,1990:50. |
| [8] | Hergenrother P M .Poly (phenylquinoxalines) containing phenylethynyl groups[J].Macromolecules,1981,14:898-904. |
| [9] | Hergenrother P M .Poly (phenylquinoxalines) containing ethynyl groups[J].Macromolecules,1981,14:891-897. |
| [10] | Connell J W;Smith Jr J G;Hergenrother P M .Chemistry and adhesive properties of phenylethynyl-terminated phenylquinoxaline oligomers[J].Journal Adhesion,1997,60:15-26. |
| [11] | Ishida Y;Ogasawara T;Yokota R .Development of highly soluble addition-type imide oligomers for matrix of carbon fiber composite (I): Imide oligomers based on asymmetric biphenyltetracarboxylic dianhydride and 9,9-bis(4-aminophenyl)fluorene[J].High performance polymers,2006(5):727-737. |
| [12] | Cheng Li,Zhuo Li,Jin-gang Liu,Hai-xia Yang,Shi-yong Yang.FLUORENE-BRIDGED POLYPHENYLQUINOXALINES WITH HIGH SOLUBILITY AND GOOD THERMAL STABILITY: SYNTHESIS AND PROPERTIES[J].高分子科学（英文版）,2010(06):971-980. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%