通过聚合物前驱体热解方法制备了SiBCN陶瓷,对其在1 200℃空气条件下的抗氧化性能进行了研究,并与前驱体法制得的SiCN陶瓷进行了比较.结果表明,SiBCN陶瓷经氧化10 h后样品氧化增重只有0.35%,并且样品中没有裂纹的出现,表现出良好的抗氧化性能.而同样条件下SiCN陶瓷氧化增重达到3.1%,样品出现裂纹.样品表面元素组成分析表明,SiBCN陶瓷表面氧化物主要以SiO2形式存在,而SiCN陶瓷表面主要以SiOx(x<2)存在.
参考文献
[1] | Paolo Colombo;Gabriela Mera;Ralf Riedel;Gian Domenico Soraru .Polymer-Derived Ceramics: 40 Years of Research and Innovation in Advanced Ceramics[J].Journal of the American Ceramic Society,2010(7):1805-1837. |
[2] | Kroke E;Li Y;Konetschny C et al.Silazane derived ceramics and related materials[J].Materials Science and Engineering,2000,26:97-199. |
[3] | Dhamne, A;Xu, WX;Fookes, BG;Fan, Y;Zhang, LG;Burton, S;Hu, JZ;Ford, J;An, LA .Polymer-ceramic conversion of liquid polyaluminasilazanes for SiAlCN ceramics[J].Journal of the American Ceramic Society,2005(9):2415-2419. |
[4] | 张立功,范翊,罗劲松,褚明晖,Wang Yiguang,Lavanya Bharadwaj,安立楠.抗氧化和抗高温腐蚀的Si-Al-C-N 聚合物前驱体陶瓷[J].稀有金属材料与工程,2005(z1):486-489. |
[5] | Francis, A;Ionescu, E;Fasel, C;Riedel, R .Crystallization Behavior and Controlling Mechanism of Iron-Containing Si-C-N Ceramics[J].Inorganic Chemistry: A Research Journal that Includes Bioinorganic, Catalytic, Organometallic, Solid-State, and Synthetic Chemistry and Reaction Dynamics,2009(21):10078-10083. |
[6] | Zheng ZM.;Li YM.;Luo YM.;Su SX.;Zhang ZJ.;Yang SY.;Gao W.;Xie ZM. .Synthesis and pyrolysis of Ti-containing precursors for advanced Si/C/N/Ti-based ceramics[J].Journal of Applied Polymer Science,2004(4):2733-2739. |
[7] | Atanu Saha;Sandeep R. Shah;Rishi Raj .Amorphous Silicon Carbonitride Fibers Drawn from Alkoxide Modified Ceraset~(TM)[J].Journal of the American Ceramic Society,2003(8):1443-1445. |
[8] | Riedel R.;Dressler W.;Ruwisch L.;Bill J.;Aldinger F.;Kienzle A. .A SILICOBORON CARBONITRIDE CERAMIC STABLE TO 2,000-DEGREES-C[J].Nature,1996(6594):796-798. |
[9] | Baldus H P;Jansen M;Sporn D .Ceramic fiber for matrix composites in high-temperature engine applications[J].Science,1999,285:699-703. |
[10] | Kumar R;Cai Y;Gerstel P;Rixecker G;Aldinger F .Processing, crystallization and characterization of polymer derived nano-crystalline Si-B-C-N ceramics[J].Journal of Materials Science,2006(21):7088-7095. |
[11] | Zhang, Z.;Zeng, F.;Han, J.;Luo, Y.;Xu, C. .Synthesis and characterization of a new liquid polymer precursor for Si-B-C-N ceramics[J].Journal of Materials Science,2011(18):5940-5947. |
[12] | Butchereit E;Nickel K G;Müller A .Precursor-derived Si-B-C-N ceramics:oxidation kinetics[J].Journal of the American Ceramic Society,2001,84(10):2184-2188. |
[13] | 吕志杰,赵军,艾兴.Si3N4/TiC纳米复合陶瓷刀具材料氧化行为[J].硅酸盐学报,2008(02):210-214. |
[14] | Wang Y;Fan Y;An L et al.Polymer-derived SiAlCN ceramics resist oxidation at 1400℃[J].Scripta Materialia,2006,55:295-297. |
[15] | Baldus H P;Passing G .Studies on SiBN(C) ceramics:oxidation and crystallization behaviour lead the way to appliction[J].Materials Research Society Symposium Proceedings,1994,346:617-622. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%