研究了A3钢和GH1131高温合金两种材料作为模具对TC4钛合金HIP组织的影响.结果表明在HIP过程中,A3钢模具对有效应力传递的阻碍作用较大,设计HIP用A3钢模具时应避免深型腔结构,GH1131模具对有效应力传递的影响较小.受元素互扩散的影响,两种模具材料在HIP过程中均污染了TC4材料表面,A3钢模具对合金的影响层较薄,但使材料形成了波浪形的粗糙表面；GH1131对成形材料的影响层厚度＞100 μm.为了获得高精度的无污染表面,TC4合金HIP净成形时两种模具均需要进行表面处理,形成与TC4兼容的保护层.
参考文献
| [1] | D.P. DFLO;H.R. PIEHLER .EARLY STAGE CONSOLIDATION MECHANISMS DURING HOT ISOSTATIC PRESSING OF Ti-6Al-4V POWDER COMPACTS[J].Acta materialia,1999(9):2841-2852. |
| [2] | Li W B;Ashby M F;Easterling K E .On densification and shape change during hot isostatic pressing[J].Acta Metallurgy,1987,35:2831-2842. |
| [3] | Songm M C;Kim H G;Kim K T .Creep densification of copper powder compact[J].Int J Mech Sic,1996,38(11):1197-1208. |
| [4] | Seliverstov D;Samarov V;kratt E .Development and manufacture of "net shape" critical rotating parts for rocket propulsion systems from Ni-base superalloy[AIAA-99-2898][R]. |
| [5] | Guichard D;Laithier F;Founier J P .Development of powder metallurgy impellers for vinci hydrogen turbopump[AIAA 2000-3831][R]. |
| [6] | Y. C. Jeon;K. T. Kim .Near-net-shape forming of 316L stainless steel powder under hot isostatic pressing[J].International Journal of Mechanical Sciences,1999(7):815-830. |
| [7] | Olevsky E.;Van Dyck S.;Froyen L.;Delaey L.;Buekenhout L.;Maximenko A. .Container influence on shrinkage under hot isostatic pressing - I. Shrinkage anisotropy of a cylindrical specimen[J].International Journal of Solids and Structures,1998(18):2283-2303. |
| [8] | D. P. DELO;R. E. DUTTON;S. L. SEMIATIN .MODELING OF HOT ISOSTATIC PRESSING AND HOT TRIAXIAL COMPACTION OF Ti-6Al-4V POWDER[J].Acta materialia,1999(11):3159-3167. |
| [9] | Hyoung Seop Kim .Densification mechanisms during hot isostatic pressing of stainless steel powder compacts[J].Journal of Materials Processing Technology,2002(2):319-322. |
| [10] | Advances in Net-Shape Powder Metallurgy[OL].http://www.afrl.af.mil/techconn/index.htm.Reference document ML03-18 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%