对退火处理后的Ti-55531钛合金α片层宽度、β晶粒尺寸、晶界α相不连续度和针状α相比例等特征进行了定量表征和统计分析,探讨了随着退火温度的升高,Ti-55531钛合金显微组织及其力学性能的相关性.结果表明,在β相区退火处理,退火温度的升高将引起晶内α片粗化长大,平均β晶粒尺寸从86μm增大到210 μm,晶界不连续度降低,针状α相的相比例先降低后升高.β晶粒尺寸与延伸率、静韧度、裂纹形成功负相关,与裂纹扩展功正相关;晶界不连续度与静韧度正相关;针状α相比例与屈服强度正相关.
参考文献
| [1] | Duret N.Titanium for damage tolerance application s on A 380[A].Hamburg:DGM,2003 |
| [2] | Warchomicka, F.;Poletti, C.;Stockinger, M. .Study of the hot deformation behaviour in Ti-5Al-5Mo-5V-3Cr-1Zr[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(28):8277-8285. |
| [3] | Tetyukhin V V;Zakharov J I;Levin I V .Titaniumbased alloy and method of heat treatment of large-sized semifinished items of this alloy[P].U.S.Patent 7,332,043,2008-2-19. |
| [4] | Jéróme Pora.A380结构的先进材料和技术--未来发展的技术平台[J].航空维修与工程,2003(6):50-52. |
| [5] | Takashi Maeda;Yoshihisa Shirai.Superplasticity in the Aerospace Titanium Alloy Ti-5553[J].Materials Science Forum,2013:140-145. |
| [6] | R. R. Boyer;R. D. Briggs .The Use of β Titanium Alloys in the Aerospace Industry[J].Journal of Materials Engineering and Performance,2005(6):681-685. |
| [7] | Robert D .Briggs,Auburn.Tough,high-strength titanium alloys;methods of heat treating titanium alloys[P].U.S.Patent 7,785,429,2010-8-31. |
| [8] | 付艳艳;惠松骁;叶文君 等.冷却速度对VST55531钛合金的显微组织和力学性能的影响[J].中国有色金属学报,2010,20(S1):685-689. |
| [9] | 葛鹏,赵永庆,周廉.热处理对1种新型亚稳定β钛合金组织与性能的影响[J].稀有金属材料与工程,2004(09):968-971. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%