利用热蒸发法在硅衬底上合成了二氧化锡纳米梭阵列,并研究其场致电子发射特性.研究结果表明,所合成的二氧化锡纳米梭是一种新型的纳米结构,可以通过反应时间的不同得到不同密度的二氧化锡纳米梭阵列,从而实现可控生长.在研究场致电子发射方面,我们发现所合成的二氧化锡纳米梭阵列有优良的场发射性能,开启电场为1.4 V/μm,对应的发射电流密度为10 μA/cm2;当电场强度为7.4 V/μm时,发射电流密度高达2.48 mA/cm2.这是由于二氧化锡纳米梭结构有很小的尖端曲率半径以及所测量样品中二氧化锡纳米梭阵列分布比较均匀造成的.测量结果发现在F-N曲线上呈现两个线性段,我们认为这是由于在不同的电场下,发射电流由不同高度的梭形结构引起的,不同高度的梭形结构由于长径比不同因而具有不同的场增强因子,从而导致在F-N曲线上表现为两个线性段.
参考文献
| [1] | Neri G.Bonavita A,Rizzo G,et al.Towards enhanced performances in gas sensing:SnO2 based nanocrystalline oxides application[J].Sensors and Actuators B,2007,122(2):564-571. |
| [2] | Park Y J,Park K S,Kim J G,et al.Characterization of tin oxide/LiMn2O1 thin-film cell[J].J.Power Sources,2000,88(2):250-254. |
| [3] | Zhang Q H,Saraf L V,Hua F.Transparent thin-film transistor with self-assembled nanocrystals[J].Nanotechnology,2007,18(19):195204(1-5). |
| [4] | Chen Y J,Nie L,Xue X Y,et al.Linear ethanol sensing of SnO2 nanorods with extremely high sensitivity[J].Appl.Phys.Lett.,2006,88(8):083105(1-3). |
| [5] | Comini E,Faglia G,Sberveglieria G.Stable and highly sensitive gas sensors based on semiconducting oxide nanobelts[J].Appl.Phy.Lett.,2002,81(10):1869-1871. |
| [6] | Liao L,Xu Z,Liu K H,et al.Large-scah aligned silicon earbonitride nanotube arrays:Syntheis,characterization,and field emission property[J].J.Appl.Phys.,2007,101(11):114306(1-3). |
| [7] | Wang X D.Zhou J,Lao C S,et al.In situ field emission of density-controlled ZnO nanowire arrays[J].Advanced Materials,2007,19(12):1627-1631. |
| [8] | Chen Y J,Li Q H,Liang Y X,et al.Field-emission from long SnO2 nanobelt arrays[J].Appl.Phy.Lett.,2004,85(23):5682-5684. |
| [9] | Wang R C,Liu C P,Huanga J L.ZnO nanopencils:Efficient field emitters[J].Appl.Phy.Lett.,2005,87(1):013110(1-3). |
| [10] | Deshpande A C,Koinkar P M,Ashtaputre S S,et al.Field emission from oriented tin oxide rods[J].Thin Solid Films,2006,515(4):1450-1454. |
| [11] | Sun S H.Meng G W,Zhang M G,et al.Synthesis of SnO2 nanostructures by carbothermal reduction of SnO2 powder[J].J.Phys.D;Appl.Phys.,2004,37(3):409-412. |
| [12] | Zhong D Y,Zhang G Y,Liu S.Universal field-emission model for carbon nanotubes on a metal tip[J].Appl.Phy.Lett.,2002,80(3):506-508. |
| [13] | 田进寿,李冀,王俊锋,等.碳纳米管场发射特性研究[J].光子学报,2003,32(12):1442-1446. |
| [14] | Marcus R B,Ravi T S,Gmitter T.Atomically sharp silicon and metal field emitters[J].IEEE Transactions on Electron Devices,1991,38(10):2289-2293. |
| [15] | Luo S H,Wan Q,Liu W L,et al.Vacuum electron field emission from SnO2 nanowhiskers synthesized in N2 and O2 atmospheres[J].Appl.Phys.Lett.,2008,88(1),013109(1-3). |
| [16] | 李英爱,刘立华,何志,等.氮化铝薄膜的厚度对场发射特性的影响[J].液晶与显示,2006,21(4),379-383. |
| [17] | 陈婷,郭平生,王莉莉,等.表面形貌特殊的碳纳米管薄膜及其场发射增强[J].液晶与显示,2007,22(3):287-292. |
| [18] | 倪赛力,常永勤,龙毅,等.氧化锌纳米棒场发射性能研究[J].物理学报,2006,55(10):5410-5412. |
| [19] | Wand Z L,Wang Q,Li J J,et al.The field emission properties of high aspect ratio diamond tips arrays and their emission properties[J].Diumond and Related Materials,2006,15(48):631-634. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%