电泳法是一种新型的大面积碳纳米管场发射阴极制备方法.文章在成功地用电泳法制备了适用于场发射显示器的碳纳米管阴极基础上,通过选用不同的碳纳米管原料、改变电泳条件等方法,进一步优化碳管阴极的性能.使用不同方法制备的碳纳米管配置电泳液,由于制备方法和碳管本身的特性,管子在电泳溶液中呈现不同的分散性.碳管管径较粗时由于表面自由能相对小,所以碳管在溶液中不易形成团聚物,电泳沉积的阴极会均匀平整;管径小的碳管则由于容易团聚,需要加入表面活性剂来改善其在电泳溶液中的分散性.场发射特性和发光显示图实验结果发现,即使得到相同均匀平整的阴极,但是由于碳管本身的发射能力的差异性最终导致电泳沉积得到的阴极的场发射特性的不同.另外,电泳的实验条件也会对沉积的阴极的场发射性能和形貌产生影响.在不同电泳直流电压条件下,碳管薄膜的密度分布和厚度不同,呈现出不同的场发射能力,结果表明当电压值在25 V时可以得到性能最佳的场发射阴极.
参考文献
| [1] | Li Y J,Sun Z,Lau S P,et al.Carbon nanotube films prepared by thermal chemical vapor deposition at low temperature for field emission applications[J].Appl.Phys.Lett.,2001,79(11):1670-1672. |
| [2] | Bonard J M,Salvetat J P,St(o)ckli T,et al.Field emission from single-wall carbon nanotube films[J].Appl.Phys.Lett.,1998,73(7):918-920. |
| [3] | Wang Q H,Corrigan T D.Dai J Y,et al.Field emission from nanotube bundle emitters at low fields[J].Appl.Phys.Lett.,1997,70(24):3308-3310. |
| [4] | Taylor W.Printed FEDs-technical advances and manufacturing cost modelling[C]//14th IV MC,California,USA:lDMC,2001:77-79. |
| [5] | Tuck R.A printable large-area FEDs[C]//SID 2000 Digest,San Francisco,USA:SID,2000:14-16. |
| [6] | Walt A de Heer,Chatelain A D,Ugarte A carbon nanotube field-emission electron source[J].Science,1995,270(17):1179-1180. |
| [7] | 姚远昭,吴裕功.新型碳纳米管场发射显示器自会聚阴极的计箅机模拟[J].液晶与显示,2006,21(6):636-639. |
| [8] | Young Chu Choi,Young Min Shin,Dong Jae Bae,el al.Patterned growth and field emission properties of vertically aligned carbon nanotubes[J].Diam.& Relat.Mater.,2001,10(8):1457-1464. |
| [9] | Cho T R,Lee J H,Song Y H,et al.Photolithography-based carbon nanotubes patterning for field emission displays[J].Mater.Sci.Eng.B,2001,79(2):128-132. |
| [10] | Murakami H,Hirakawa M,Tanaka C,et al.Field emission from well-aligned,patterned,carbon nanotube emitters[J].Appl.Phys.Lett.,2000,76(13):1776-1778. |
| [11] | 李玉魁,郭艳清,朱长纯.三极结构场致发射显示器件的制作[J].液晶与显示,2006,21(3):232-235. |
| [12] | Li J T,Lei W,Zhang X B,et al.Field emission characteristic of screen-printed carbon nanotube cathode[J].Appl.Surf.Sci.,2003,220(1):96-104. |
| [13] | Shi Y S,Zhu C C,Wang Q K,et al.Large area screen-printing cathode of CNTs for FED[J].Diam.& Relat.Mater.,2003,12(9):1449-1452. |
| [14] | 朱长纯,刘兴辉.碳纳米管场发射显示器的研究进展[J].发光学报,2005,26(5):557-563. |
| [15] | 黄岱,罗淑云.单色FED荧光屏的研制与分析[J].清华大学学报:自然科学版,1999,39(1):26-29. |
| [16] | Yum J H,Kim S S,Sung Y E.Y3Al5O12:Ce0.05 phosphor coatings on a flexible substrate for use in white lightemitting diodes[J].Coll.& Sur f.A:Physicochem.Eng.Aspects,2004,251(1-3):203-207. |
| [17] | Baea J C,Yoona Y J,Leeb S J H,et al.Field emission properties of carbon nanotubes deposited by electrophoresis[J].Physica B,2002,323(1):168-170. |
| [18] | Du C S,Heldbrant D,Pan N.Preparation and preliminary property study of carbon nanotubes films by electrophoretic deposition[J].Mate.Lett.,2002,57(1):434-438. |
| [19] | Kurnosov D A,Baturin A S.Bugaev A S,et al.Influence of the interelectrode distance in eleetrophoretic cold cathode fabrication on the emission uniformity[J].Appl.Surf.Scie.,2003,215(1):232-236. |
| [20] | Choi W B,Jin Y W,Kim H Y,et al.Electrophoresis deposition of carbon nanotubes for triode-type field emission display[J].Appl.Phys.Lett.,2001,78(11):1547-1549. |
| [21] | 王莉莉,孙卓,陈婷,等.电泳法制备碳纳米管场发射阴极的研究[J].真空科学与技术学报,2006,26(1):4-7. |
| [22] | 张兆祥,张耿民,侯士敏,等.碳纳米管的薄膜场发射[J].真空科学与技术学报,2003,23(1):27-32. |
| [23] | 赵晓雪,张耿民.薄膜场发射阴极中纳米线密度的理论优化[J].真空科学与技术学报,2002,22(5):357-360. |
| [24] | Choi W B,Chung D S,Kang J H,et al.Fully sealed,high-brightness carbon-nanotube field-emission display[J].Appl.Phys.Lett.,1999,75(20):3129-3131. |
| [25] | Groning O,Küttel O M,Emmenegger C,et al.Field emission properties of carbon nanotubes[J].J Vac.Sci.Technol.B,2000,18(2):665-668. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%