为了探讨(3-545T超薄层的发光特性,设计了结构为:ITO/2T-NATA(20 nm)/NPBX(20 nm)/C-545T(d nm)/BCP(8 nm)./Alq(40 nm)/LiF(0.5 nm)/Al的绿光器件.结果表明,随着C-545T层厚度d的增加,器件的亮度和效率均下降,这是由于C-545T染料的浓度淬灭效应引起的.在此基础上,制备了基于C-545T超薄层为发光层之一的多层结构的白光器件,器件结构为:ITO/NPBX(30 nm)/Rubrene(0.2 nm)/NPBX(5 nm)/DPVBi (20 nm)/NPBX(4 nm)/C-545T(0.1 nm)/Alq(30 nm)/LiF(0.5 nm)/Al.在驱动电压为16 V时,其最大亮度达到12 320 cd/m2,对应的色坐标为(0.32,0.40),在电压为4 V时,最大光功率效率达到了3.45 lm/w.
参考文献
| [1] | Deshpande R S,Bulovic'V,Forrest S R.White-light-emitting organic electroluminescent devices based on interlayer sequential energy transfer[J].Appl.Phys.Lett.,1999,75(7):888-890. |
| [2] | Huang Y S,Jou J H,Weng W K,et al.High-efficiency white organic light-emitting devices with dual doped structure[J].Appl.Phys.Lett.,2002,80(15):2782-2784. |
| [3] | D'Andrade B W,Thompson M E,Forrest S R.Controlling exciton diffusion in muhilayer white phosphorescent organic light emitting devices[J].Adv.Mater.,2002,14(2):147-151. |
| [4] | Chen Chin H,Tang Ching W.Efficient green organic light-emitting diodes with stericly hindered coumarin dopants[J].Appl.Phys.Lett.,2001,79(22):3711-3713. |
| [5] | Xiuling Zhu,Jiaxin Sun,Huajun Peng,et.al.Inverted top-emitting organic light-emitting devices using vanadium pentoxide as anode buffer layer[J].SID Digest,2005,36(1):793-795. |
| [6] | 钟建,成建波,陈文彬,等.发光层掺杂多层结构绿色OLED光电性能研究l-J].光电工程,2006,33(9):128-132. |
| [7] | Culligan By Sean W,Chen Andrew C A,Wallace Jason U,et.al.Effect of hole mobility through emissive layer on temporal stability of blue organic light-emitting diodes[J].Adv.Funct.Mater.,2006,16(11);1481-1487. |
| [8] | 黄春辉,李富友,黄纬.有机电致发光材料与器件导论[M].上海:复旦大学出版社,2005:214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%