以H2O2陈化处理的锌粉为原料,采用高温气相反应法,在管式炉中制备四脚状氧化锌,并用扫描电镜和X射线能谱仪对产物进行了表征.通过场致发射性能测试和场致发射显示的实验,表明四脚状ZnO是一种良好的场致发射阴极材料.
参考文献
[1] | Fuller M L.Twinning in zinc oxide[J].J.Appl.Phys.,1994,15(2):164-170. |
[2] | Fujii M,Iwanaga H,Ichihara M,et al.Structure of tetrapod-like ZnO crystals[J].J.Cryst.Growth.,1993,128(1):1095-1098. |
[3] | 陈尔凡,田雅娟,程远杰,等.四脚状氧化锌晶须的生长习性及机理的研究[J].硅酸盐学报,2001,(2):151-156. |
[4] | 李树尘.碳还原剂控制氧化锌生产工艺方法:中国专利,1101952A[P].1995-04-26. |
[5] | 范兴祥,彭金辉,张利波,等.微波辐射法制备四角状氧化锌晶须的新工艺研究[J].化工矿物与加工,2004,33(6):13-14,37. |
[6] | Hu J Q,Ma X L,Xie Z Y,et al.Characterization of zinc oxide crystal whiskers grown by thermal evapo ration[J].Chem.Phys.Lett.,2001,344(1):97-100. |
[7] | Higashi Y,Eizo A,Toshihiro M,et al.Zinc oxide whiskers having a tetrapod eystalline form and method for making the same:Ep 0324797 A 1[P].1988-08-02. |
[8] | Li Q H,Wan Q,Chen Y J,et al.Stable field emission from tetrapod-like ZnO nanostructures[J].Appl.Phys.Lett.,2004,85(4):636-638. |
[9] | 陈尔凡,田雅娟,程远杰,等.四脚状氧化锌晶须制备及微观形态的研究[J].高等学校化学学报,2000,(2):172-176. |
[10] | Wan Q,Yu K,Wang T H.Low-field electron emission from tetrapod-like ZnO nanostructures synthesized by rapid evaporation[J].Appl.Phys.Lett.,2003,83(11):2253-2255. |
[11] | Baylor L R,Merkulov V I,Ellis E D.Field emission from isolated individual vertically aligned carbon nanocones[J].J.Appl.Phys.,2002,91(7):4602-4606. |
[12] | Dong L,Jiao J,Tuggle D W.ZnO nanowires formed on tungsten substrates and their electron field emission properties[J].Appl.Phys.Lett.,2003,82(7):1096-1098. |