采用一种既具有空穴传输特性又具有发光特性的新型荧光染料(E)-2-(4-(dipheny-lamino)styryl)quinolato-zinc (TPAHQZn)作为发光层,制备了结构为 ITO/ 4,4′,4″-{N,-(2-naphthyl)-N-phenylamino}-triphenylamine (2T-NATA)(15 nm)/ (E)-2-(4-(diphenylamino)styryl)quinolato-zinc (TPAHQZn)(x nm)/9,10-bis(2-naphthyl)anthracene(ADN)(31 nm)/ tris(8-quinolinolato) aluminum(Alq3)((65-x) nm)/LiF(0.6 nm)/Al的黄色有机电致发光器件.研究了不同厚度的发光层对器件性能的影响.TPAHQZn厚度为30 nm 的器件在14 V电压下实现了黄光发射,最大发光亮度为 2 479 cd/m2,最大电流效率为0.84 cd/A,色坐标由8 V(6.346 cd/m2)时的(0.502,0.449 5)到14 V(2 479 cd/m2 )时的(0.497 9,0.453)变化不大,器件的发光颜色稳定.
参考文献
| [1] | Kido J,Ohtaki C,Hongawa K,et al.1,2,4-triazole derivative as an electron transport layer in organic electroluminescent devices[J].Jpn.J.Appl.Phys,Part 2,1993,32(7A):917-920. |
| [2] | Hamada Y,Sano T,Fujita M,et al.Electrically switchable mesoscale Penrose quasierystal structure[J].Jpn.J.Appl.Phys.,Part 2,1993,32(4A):514-520. |
| [3] | Hamada Y,Sano T,Fujii H,et al.White light-emitting material for organic electro-luminesecent devices[J].Jpn.J.Appl.Phys.,1996,35(10B):1339-1341. |
| [4] | Sharma A,Singh D,Makrandi J K,et al.Electroluminescent characteristics of OLEDs fabricated with bis(5,7-dichloro-8-hydroxyquinolinato)zinc(II) as light emitting material[J].Mater.Lett.,2007,61(23-24):4614-4617. |
| [5] | Pohl R,Montes V A,Shinar J.Red-green-blue emission from tis(5-aryl-8-quinelinolate)Al(Ⅲ) complexes[J].Org.Chem.,2004,69(5):1723-1725. |
| [6] | Barberis V P,Mikroyannidis J A.Synthesis and optical properties of aluminum and zinc quinolates through styryl subsituent in 2-position[J].Synth Met.,2006,156(11-13):865-871. |
| [7] | Ding G Y,Jiang W L,Wang J,et al.White organic light-emitting devices based on novel (E)-2-(4-(diphenylamino) styryl)quinolato zinc as a hole-transporting emitter[J].Semicond.Sci.Technol.,2009,24(2):025016(1-5). |
| [8] | Chen P.Stadies on white organic light emitting devices based on blue fluorescence and orange phosphorescence[D].Changchun:Jilin University,2008. |
| [9] | Tse S C,So S K,Yeung M Y,et al.The role of charge-transfer integral in determining and engineering the carrier mobilities of 9,10-di(2-naphthyl)anthracene compounds[J].Chem.Phys.Lett.,2006,422(4-6):354-357. |
| [10] | Culligan S W,Andrew Chen C A,Wallace J U,et al.Effect of hole mobility through emissive layer on temporal stability of blue organic light-emitting diodes[J].Advancde Function Materials,2006,16(11):1481-1487. |
| [11] | 黄春辉,李富友,黄纬.有机电致发光材料与器件导论[M].上海:复旦大学出版社,2005:145. |
| [12] | Huang J S,Yang K X,Liu S Y,et al.High-brightness organic double-quantum-well electroluminescent device[J].Appl.Phys.Lett.,2000,77(12):1750-1752. |
| [13] | 丁桂英,汪津,王广德,等.基于rubrene掺杂剂的高亮度白色有机电致发光器件[J].液晶与显示,2008,23(1):5-10. |
| [14] | 丁桂英,姜文龙,汪津,等.利用C-545T超薄层多层结构的白光器件[J].液晶与显示,2008,23(2):214-218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%