本文研究了共掺Er3+/Yb3+P2O3-B2O3-Al2O3-SrO-BaO玻璃的能量转移过程.实验中制备了高掺杂Yb3+离子的双掺Er3+/Yb3+的磷酸盐玻璃样品.在Er3+/Yb3+掺杂比率>1:18(mol%)时,观测到了基于Yb3+离子至Er3+离子能量转移下Er3+(4I13/2→4I15/2)的增强发射和Yb3+(2F7/2→2F5/2)发射的减弱,当Yb3+离子掺杂浓度超过2.1×1021ions/cm3时(Er3+/Yb3+≤1:18,mol%),由于Yb3+离子的自淬灭效应,Er3+离子的发射强度降低.实验中得到了Yb3+离子的最佳掺杂浓度为1.74×1021ions/cm3.
Energy transfer study has been made in Er3+ /Yb3+ cooped P2O3- B2O3- Al2O3- SrO- BaO glasses. Er3+ /Yb3+ codoped phosphate glass samples were prepared with high concentration of Yb3+ ions. Enhancement of Er3+ (4I13/2→ 4I15/2)emission and a decrease in the Yb3+ emission (2F7/2 → 2F5/2) can be observed when the doping concentration ratio Er3+ /Yb3+ is >1:18 (mol% ) as a result of energy transfer from Yb3+ ions to Er3+ ions. When the concentration of Yb3+ ions is high enough (NYb>2.1× 1021ions/cm3, Er3+ /Yb3+ ≤ 1:18, mol% ), emission intensity of Er3+decreases due to the radiative trapping of Yb3+ ions. The best doping concentration of Yb3+ ion was found to be approximately 1.74× 1021ions/cm3.
参考文献
[1] | GAPONTSEV V P;MATISIN S M;ISINEEV A A et al.[J].Optics & Laser Technology,1982,14:189. |
[2] | HAMLIN S J;MYERS J D;MYERS M J .[J].SPIE,1991,1419:100. |
[3] | LUKAC M;MARINCEK M .[J].IEEE Journal of Oceanic Engineering,1990,26:1779. |
[4] | ADAM J L;LUCAS J;JIANG S B .[J].SPIE,1995,2996:13. |
[5] | AUZEL E E .[J].Proceedings of the IEEE,1973,61:758. |
[6] | Joshi BC;Lohani R .Non-radiative energy transfer from Tm3+ to Ho3+ and Nd3+ in zinc phosphate glass[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1997(1):103-107. |
[7] | LAPORTA P;DESIIVESTRI S;MAGNI V et al.[J].Optics Letters,1991,16:1952. |
[8] | SUMIDA D S;FAN T Y .[J].Optics Letters,1994,19:1343. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%