主要报导了热解碳的氮离子注入处理、等离子体浸没离子注入及其血液相容性.用卢瑟福背散射、X射线衍射和喇曼光谱法分析样品的成份及结构.测试了注入前后热解碳样品的血小板粘附性能,经过注入处理的样品表面粘附较少的血小板,而且较少团簇及变形,优于临床应用的热解碳.蛋白质竞争吸附实验结果表明热解碳经PIII处理后,表面会吸附较多的白蛋白、较少的纤维蛋白原,具有更好的抗凝血性能.
参考文献
[1] | Baurschmidt P;Schaldach M .[J].Medical and Biological Engineering and Computing,1980,18:496. |
[2] | Bolz A;Schaldach M .[J].Artificial Organs,1990,14:260. |
[3] | Matamura Y et al.[J].JOURNAL OF BIOMATERIALS APPLICATIONS,1989,4(11):33. |
[4] | Olin C;Johansson E .[P].PCT Int Appl,WO 9533501,Dec 14,1995. |
[5] | Dion I;Rouais F et al.[J].Biomaterials,1993,14(03):169. |
[6] | Kim S W;Wisniewski S et al.[J].Journal of Biomedical Materials Research Symposium,1977,8:23. |
[7] | Thomson A;Law F C et al.[J].Biomaterials,1991,12(01):37. |
[8] | Evans A C.[J].Medical Device Technology,1991 |
[9] | Zheng C Q et al.[Z].Berlin,1992. |
[10] | 田子林;陈匡民 等.[J].中华胸心血管外科杂志,1992,8(01):1. |
[11] | Dion I;Roques X et al.[J].Biomedical Materials & Engineering,1993,5:51. |
[12] | Lankford J et al.[J].Nuclear Instruments and Methods in Physics Research,1993,80/81:1441. |
[13] | DEARNALEY G et al.[J].Surface Engineering,1991,7(02):127. |
[14] | Huang N;Liu X H et al.[J].Journal of Boimater Appl,1994,8:204. |
[15] | Zhang F;Huang N et al.[J].Surface and Coatings Technology,1996,84:476. |
[16] | Zhang Feng;Chen Yu et al.[J].中国科学C辑(英文版),1998,41(04):400. |
[17] | Wang X H;Feng Zhang et al.[J].Surface and Coatings Technology,2000,128/129:36. |
[18] | Dollittle L R .9[J].Nuclear Instruments and Methods in Physics Research,1985,B9:344. |
[19] | Li C R;Manova D.7th Inter Conf on Plasma Surf Eng (7PSE)[M].Germany: Garmisch-Partenkirchen,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%