用差热分析(DTA),结合X射线衍射(XRD)研究了非晶Pr8Fe86B6合金的晶化动力学.结果表明:该非晶Pr8Fe86B6合金的晶化相为α-Fe固溶体、Pr2Fe23B3和Pr2Fe14B金属间化合物,通过对三相晶化激活能的分析得出:α-Fe相的激活能在晶化初期变化不大,当其体积分数大于8%时,其晶化激活能开始减小;而Pr2Fe23B3和Pr2Fe14B相的激活能随其体积分数的增加而减小,且α-Fe相较Pr2Fe23B3和Pr2Fe14B相容易晶化析出.
参考文献
[1] | Ralph Skomski;Coey J D .[J].Physical Review,1993,B48:15812. |
[2] | Chang WC.;Wu SH.;Ma BM.;Bounds CO.;Chiou DY. .High performance alpha-Fe/Nd2Fe14B-type nanocomposites[J].Applied physics letters,1998(1):121-123. |
[3] | Ding J;McCormicks P G;Street R .[J].Journal of Magnetism and Magnetic Materials,1993,124:1. |
[4] | Schrefl T.;Fidler J. .Micromagnetic simulation of magnetizability of nanocomposite Nd-Fe-B magnets[J].Journal of Applied Physics,1998(11 Pt.2):6262-6264. |
[5] | Schrefl T;Fidler J;Kronmü ller H .[J].Physical Review,1994,B49:6100. |
[6] | 高文莉;隋智通;卢柯 .非晶态Pb-Cu-Si合金的晶化动力学研究[J].金属学报,1992,7:B304. |
[7] | Zhang J W;Zhang X Y;Xiao F R et al.[J].Materials Letters,1998,36:233. |
[8] | Zhang X Y;Zhang K Q;Liu J H et al.[J].Journal of Applied Physics,2001,89:1. |
[9] | Kissinger H E .[J].Analytical Chemistry,1975,29:1702. |
[10] | 李余增.热分析[M].北京:清华大学出版社,1987:82. |
[11] | 王佐诚,乔祎.纳米复合Pr2(FeZr)14B/α-Fe永磁合金[J].金属功能材料,1998(02):65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%