Ni/MH电池负极的高倍率性能和低温放电性能的提高应当受到重视.采用廉价的硼镍合金(B-Ni)作为掺硼添加剂,有效地改善常用MlNi3.55Co0.75Mn0.4Al0.3贮氢合金的高倍率性能和低温放电性能.实验结果表明,掺硼合金由于形成含CeCo4B相的复相结构可显著提高合金的电化学动力学性能,掺硼的MlNi3.55Co0.75Mn0.4Al0.3B0.3合金能够满足高功率型Ni/MH电池的高倍率性能和低温型Ni/MH电池在低温-35℃下的小倍率放电(120mA/g)的要求.
参考文献
[1] | 陈长聘,王春生.高性能贮氢电极合金[J].物理,1998(03):156. |
[2] | Otto A;Guther V .[J].Journal of Alloys and Compounds,1999,293-295:734. |
[3] | 叶辉,李志林,吴铸,向玉双,张宏.贮氢合金低温电化学性能的研究[C].第三届全国氢能学术会议论文集,2001:127-134. |
[4] | Nelson R F .[J].Journal of Power Sources,2000,91:2. |
[5] | Erbacher J K .[J].Journal of Power Sources,1999,80:265. |
[6] | Atwater T B;Cygan P J;Leung F C .[J].Journal of Power Sources,2000,91:27. |
[7] | Ye Hui;Zhang Hong;Chen Jianxia;Huang Tiesheng .[J].Journal of Alloys and Compounds,2000,308:163. |
[8] | Ye Hui;Zhang Hong;Wu Wenaquan;Huang Tiesheng .[J].Journal of Alloys and Compounds,2000,312:68. |
[9] | Notten P H L;Hokkeling P .[J].Journal of the Electrochemical Society,1991,138:1877. |
[10] | Kuriyama Nobuhiro;Sakai Tetsuo;Miyamura Hiroshi et al.[J].Journal of Alloys and Compounds,1993,202:183. |
[11] | Inoue Hiroshi;Miyamoto Masayoshi;Matsuoka Masao et al.[J].Electrochimica Acta,1997,42:1087. |
[12] | Geng M M;Han J W;FENG F et al.[J].Journal of the Electrochemical Society,1999,146:3591. |
[13] | Tadokoro M;Nogami M;Chikano Y et al.[J].Journal of Alloys and Compounds,1993,192:179. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%