用固相反应法制备了La0.5-xPrxBa0.5CoO3系列化合物,系统研究了Pr不同含量时材料的磁性和电输运特性.结果表明:Pr掺杂没有改变Co的3d电子的巡游特性.随Pr掺杂量增加,材料的分子磁矩单调下降,其原因是当Pr逐渐取代La时,Co离子的3d电子逐渐由中间自旋态向低自旋态转变.随Pr含量增加,材料的居里温度逐渐下降,这是由于稀土离子的尺寸效应.电阻测量表明:在所研究的温度范围内,居里温度以下,所有掺Pr材料的导电机制为热扩散型.居里点以上,导电机制为变程跳跃导电.
参考文献
[1] | Mukherjee S;Raychaudhuri P;Nigam A K .[J].Physical Review B,2000,61:8651. |
[2] | Troyanchuk IO.;Khalyavin DD.;Szymczak H.;Szymczak R.;Baran M.;Kasper NV. .Magnetic and electrical transport properties of orthocobaltites R0.5Ba0.5CoO3 (R = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy)[J].Physical Review.B.Condensed Matter,1998(5):2418-2421. |
[3] | Yamaguchi S;Okimoto Y;Tokura Y .[J].Physical Review B,1997,55:R8666. |
[4] | Zhuang M.;Ming NB.;Zhang WY. .Competition of various spin states of LaCoO3[J].Physical Review.B.Condensed Matter,1998(17):10705-10709. |
[5] | Asai K;Yokokura O;Nishimori N et al.[J].Physical Review B,1994,50:3025. |
[6] | Wholfarth E P.[J].Journal of Magnetism and Magnetic Materials,1978(07):113. |
[7] | Jin S;McCormac M;Tiefel T H .[J].Journal of Applied Physics,1994,76(15):6929. |
[8] | 戴道生;钱昆明.铁磁学[M].北京:科学出版社,1992 |
[9] | Young Sun;Xiaojun Xu;Yuheng Zhang .[J].Physical Review B,2000,62:5289. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%