研究了纳米金红石型TiO2经空气和氨气气氛热处理后其光催化性能的变化.利用UV-VIS分光光度计,X射线衍射(XRD)和X射线光电子能谱(XPS)等技术对热处理前后的样品进行了表征.结果表明:在紫外和可见光照射下,NH3中525℃热处理和空气中600℃热处理所得样品的光催化性能比未经处理的样品分别提高了30%和60%.样品在热处理前后晶体结构和晶粒大小都未发生变化.氨气中热处理的样品含有微量的氮元素.
参考文献
| [1] | 周铭.纳米二氧化钛研究进展[J].涂料工业,1996(04):36-39. |
| [2] | ZHANG Qin - hong;GAO Lian;GUO Jin - kun .Effect of calcinations on the photocatalytic properties of nanosized TiO2 powders prepared by TiCl4 hydrolysis[J].Applied Catalysis B:Environmental,2000,26:207-215. |
| [3] | 王本根,李义和,王清华.Al2O3涂敷TiO2纳米晶粒的制备及其抗絮凝性研究[J].高等学校化学学报,1998(05):685-687. |
| [4] | 袁荞龙;罗宁 .国内钛白粉生产、研究及应用进展[J].化工进展,1997,5:5. |
| [5] | Fujishima A;Honda K .Photolysis- decomposition of water at the surface of an irradiated semiconductor[J].Nature,1972,238:37-38. |
| [6] | Hiroshi Tsuji;Tomohiko Sagimori;Ken' ichi Kurita et al.Surface modif ation of TiO2 (rutile) by metal negative ion implantation for improving catalytic properties[J].Surface and Coatings Technology,2002,158-159:208-213. |
| [7] | Asahi R;Morikawa T;Ohwaki T et al.Visible - Light Photocatalysis in nitrogen- doped titanium oxides[J].Science,2001,293(13):269-271. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%